Tuned sensitivity towards H{sub 2}S and NH{sub 3} with Cu doped barium strontium titanate materials
Journal Article
·
· AIP Conference Proceedings
- National Institute of Materials Physics, Atomistilor 105bis, P.O. Box MG-7, 077125, Bucharest-Magurele (Romania)
- AG Weimar, Institute of Physical and Theoretical Chemistry, University of Tübingen, Auf der Morgenstelle 15, D-72076 Tübingen (Germany)
- National R and D Institute for Non-ferrous and Rare Metals, 102 Biruintei Blvd, Ilfov (Romania)
The different amount of Cu-doped Barium Strontium Titanate (BST) thick film materials have been tested for their gas-sensing performances towards NH{sub 3} and H{sub 2}S under dry and 50% relative humidity (RH) background conditions. The optimum NH{sub 3} sensitivity was attained with 0.1mol% Cu-doped BST whereas the selective detection of H{sub 2}S was highlighted using 5mol% Cu-doped BST material. No cross-sensitivity effects to CO, NO{sub 2}, CH{sub 4} and SO{sub 2} were observed for all tested materials operated at their optimum temperature (200°C) under humid conditions (50% RH). The presence of humidity clearly enhances the gas sensitivity to NH{sub 3} and H{sub 2}S detection.
- OSTI ID:
- 22390538
- Journal Information:
- AIP Conference Proceedings, Vol. 1627, Issue 1; Conference: 14. Electroceramics Conference, Bucharest (Romania), 16-20 Jun 2014; Other Information: (c) 2014 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
The influences of mole composition of strontium (x) on properties of barium strontium titanate (Ba{sub 1−x}Sr{sub x}TiO{sub 3}) prepared by solid state reaction method
Effect of dispersant on preparation of barium-strontium titanate powders through oxalate co-precipitation method
Simple oxalate precursor route for the preparation of barium-strontium titanate: Ba{sub 1-x}Sr{sub x}TiO{sub 3} powders
Journal Article
·
Mon Feb 08 00:00:00 EST 2016
· AIP Conference Proceedings
·
OSTI ID:22390538
+1 more
Effect of dispersant on preparation of barium-strontium titanate powders through oxalate co-precipitation method
Journal Article
·
Thu Apr 02 00:00:00 EDT 2009
· Materials Research Bulletin
·
OSTI ID:22390538
Simple oxalate precursor route for the preparation of barium-strontium titanate: Ba{sub 1-x}Sr{sub x}TiO{sub 3} powders
Journal Article
·
Sat Jan 15 00:00:00 EST 2005
· Materials Characterization
·
OSTI ID:22390538
+3 more