Title: Electric field induced cubic to monoclinic phase transition in multiferroic 0.65Bi(Ni{sub 1/2}Ti{sub 1/2})O{sub 3}-0.35PbTiO{sub 3} solid solution

The results of x-ray diffraction studies on 0.65Bi(Ni{sub 1/2}Ti{sub 1/2})O{sub 3}-0.35PbTiO{sub 3} solid solution poled at various electric fields are presented. After poling, significant value of planar electromechanical coupling coefficient (k{sub P}) is observed for this composition having cubic structure in unpoled state. The cubic structure of 0.65Bi(Ni{sub 1/2}Ti{sub 1/2})O{sub 3}-0.35PbTiO{sub 3} transforms to monoclinic structure with space group Pm for the poling field ≥5 kV/cm. Large c-axis microscopic lattice strain (1.6%) is achieved at 30 kV/cm poling field. The variation of the c-axis strain and unit cell volume with poling field shows a drastic jump similar to that observed for strain versus electric field curve in (1 − x)Pb(Mg{sub 1/3}Nb{sub 2/3}) O{sub 3}-xPbTiO{sub 3} and (1 − x)Pb(Zn{sub 1/3}Nb{sub 2/3})O{sub 3}-xPbTiO{sub 3}.
Authors:
;  [1]
  1. School of Materials Science and Technology, Indian Institute of Technology (Banaras Hindu University), Varanasi 221005 (India)
Publication Date:
OSTI Identifier:
22350968
Resource Type:
Journal Article
Resource Relation:
Journal Name: Applied Physics Letters; Journal Volume: 105; Journal Issue: 16; Other Information: (c) 2014 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND SUPERFLUIDITY; BISMUTH COMPOUNDS; COUPLING; CUBIC LATTICES; ELECTRIC FIELDS; LEAD COMPOUNDS; MONOCLINIC LATTICES; NICKEL COMPOUNDS; OXYGEN COMPOUNDS; PHASE TRANSFORMATIONS; SOLID SOLUTIONS; SPACE GROUPS; STRAINS; TITANATES; TITANIUM COMPOUNDS; X-RAY DIFFRACTION