Title: Synthesis and photoluminescence properties of Ca{sub 19}Mg{sub 2}(PO{sub 4}){sub 14}:Sm{sup 3+} red phosphor for white light emitting diodes

Highlights: • A novel red phosphor Ca{sub 19}Mg{sub 2}(PO{sub 4}){sub 14}:Sm{sup 3+} was synthesized and investigated firstly. • The structure and characteristic luminescence properties are discussed. • The excellent thermal stability was found and investigated. • It has good color saturation, the CIE is close to that of commercial Y{sub 2}O{sub 3}:Eu{sup 3+}. - Abstract: A series of Sm{sup 3+} doped Ca{sub 19}Mg{sub 2}(PO{sub 4}){sub 14} red phosphors were successfully synthesized. X-ray diffraction analysis indicates that all the samples are single phased. The luminescence property is investigated in detail by measuring their photoluminescence excitation and emission spectra. Ca{sub 19}Mg{sub 2}(PO{sub 4}){sub 14}:Sm{sup 3+} phosphors show strong absorption in 400–410 nm region, which is suitable for application in LEDs. When excited at 403 nm, Ca{sub 19}Mg{sub 2}(PO{sub 4}){sub 14}:Sm{sup 3+} phosphor can emit red emission with CIE chromaticity coordinates (0.615, 0.384). The optimal doping concentration of Sm{sup 3+} doped Ca{sub 19}Mg{sub 2}(PO{sub 4}){sub 14} is measured to be 0.02. The thermal quenching property is also measured and compared with the commercial red phosphor Y{sub 2}O{sub 3}:Eu{sup 3+} (Topstar, TXC-RIA). The results indicate Ca{sub 19}Mg{sub 2}(PO{sub 4}){sub 14}:Sm{sup 3+} phosphors have potential to serve as a red phosphor for white LEDs.
Authors:
; ;  [1] ;  [2] ;  [1] ;  [2]
  1. Department of Materials Science, School of Physical Science and Technology, Lanzhou University, Lanzhou 730000 (China)
  2. (China)
Publication Date:
OSTI Identifier:
22348689
Resource Type:
Journal Article
Resource Relation:
Journal Name: Materials Research Bulletin; Journal Volume: 55; Other Information: Copyright (c) 2014 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
36 MATERIALS SCIENCE; 37 INORGANIC, ORGANIC, PHYSICAL AND ANALYTICAL CHEMISTRY; ABSORPTION; DOPED MATERIALS; EMISSION SPECTRA; EUROPIUM IONS; EXCITATION; LIGHT EMITTING DIODES; PHOSPHATES; PHOSPHORS; PHOTOLUMINESCENCE; SAMARIUM IONS; SYNTHESIS; X-RAY DIFFRACTION; YTTRIUM OXIDES