Title: Synthesis, properties and phase transitions of pyrochlore- and fluorite-like Ln{sub 2}RMO{sub 7} (Ln = Sm, Ho; R = Lu, Sc; M = Nb, Ta)

Graphical abstract: Temperature dependences of bulk conductivity for Sm{sub 2}ScTaO{sub 7} pyrochlore prepared at (1) 1400 °C, 20 h; and (2) 1200 °C, 40 h. - Highlights: • The phase formation of Ln{sub 2}RMO{sub 7} (Ln = Sm, Ho; R = Lu, Sc; M = Nb, Ta) at 1200–1600 °C. • The bulk conductivity and magnetic susceptibility were measured. • The bulk conductivity of Sm{sub 2}ScTaO{sub 7} has oxygen ion type at T ≥ 750 °C. • The first-order structural phase transition was observed in Sm{sub 2}ScTaO{sub 7} at ∼650–700 °C. • This phase transformation is not typical for defect fluorites. - Abstract: We have studied the new compounds with fluorite-like (Ho{sub 2}RNbO{sub 7} (R = Lu, Sc)) and pyrochlore-like (Sm{sub 2}ScTaO{sub 7}) structure as potential oxide ion conductors. The phase formation process (from 1200 to 1600 °C) and physical properties (electrical, thermo mechanical, and magnetic) for these compounds were investigated. Among the niobate materials the highest bulk conductivity is offered by the fluorite-like Ho{sub 2}ScNbO{sub 7} synthesized at 1600 °C: 3.8 × 10{sup −5} S/cm at 750 °C, whereas in Sm system the highest bulk conductivity, 7.3 × 10{sup −6} S/cm at 750 °C, is offered by the pyrochloremore » Sm{sub 2}ScTaO{sub 7} synthesized at 1400 °C. In Sm{sub 2}ScTaO{sub 7} pyrochlore we have observed the first-order phase transformation at ∼650–700 °C is related to rearrangement process in the oxygen sublattice of the pyrochlore structure containing B-site cations in different valence state and actually is absent in the defect fluorites. The two holmium niobates show Curie–Weiss paramagnetic behavior, with the prevalence of antiferromagnetic coupling. The magnetic susceptibility of Sm{sub 2}ScTaO{sub 7} is a weak function of temperature, corresponding to Van Vleck paramagnetism.« less
Authors:
 [1] ;  [2] ;  [1] ;  [3] ;  [1] ;  [3]
  1. Semenov Institute of Chemical Physics, Russian Academy of Sciences, ul. Kosygina 4, Moscow 119991 (Russian Federation)
  2. Faculty of Chemistry, Moscow State University, Leninskie gory 1, Moscow 119991 (Russian Federation)
  3. Emmanuel Institute of Biochemical Physics, Russian Academy of Sciences, ul. Kosygina 4, Moscow 119991 (Russian Federation)
Publication Date:
OSTI Identifier:
22341870
Resource Type:
Journal Article
Resource Relation:
Journal Name: Materials Research Bulletin; Journal Volume: 49; Other Information: Copyright (c) 2013 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
36 MATERIALS SCIENCE; ANTIFERROMAGNETISM; CATIONS; FLUORITE; HOLMIUM; IONIC CONDUCTIVITY; MAGNETIC SUSCEPTIBILITY; NIOBATES; OXIDES; OXYGEN; OXYGEN IONS; PARAMAGNETISM; PHASE TRANSFORMATIONS; PYROCHLORE; SYNTHESIS; TEMPERATURE DEPENDENCE; THERMAL EXPANSION