Title: Controlled synthesis of novel octapod platinum nanocrystals under microwave irradiation

Graphical abstract: Under microwave irradiation, novel octapod Pt nanocrystals were synthesized by reducing H{sub 2}PtCl{sub 6} in TEG with PVP as a stabilizer. The as-prepared Pt nanocrystals displayed a unique octapod nanostructure with five little mastoids in each concave center. The use of KI was crucial to the formation of novel Pt octapods. Novel Octapod Platinum Nanocrystals. - Highlights: • A novel octapod Pt nanocrystals different from the common octapod were obtained. • The use of KI was crucial to the formation of the novel Pt octapods. • Microwave was readily employed in controlled synthesis of the novel Pt octapods. - Abstract: Microwave was employed in the shape-controlled synthesis of Pt nanoparticles. Novel octapod Pt nanocrystals enclosed with (1 1 1) facets were readily synthesized with H{sub 2}PtCl{sub 6} as a precursor, tetraethylene glycol (TEG) as both a solvent and a reducing agent, polyvinylpyrrolidone (PVP) as a stabilizer in the presence of an appropriate amount of KI under microwave irradiation for 140 s. The as-prepared Pt nanocrystals displayed a unique octapod nanostructure with five little mastoids in each concave center and exhibited higher electrocatalytic activity than commercial Pt black in the electro-oxidations of methanol and formic acid. The results demonstratedmore » that the use of KI was crucial to the formation of Pt octapods. KI determined the formation of the novel octapod Pt nanocrystals by tuning up the reduction kinetics and adsorbing on the surfaces of growing Pt nanoparticles. The optimum molar ratio of H{sub 2}PtCl{sub 6}/KI/PVP was 1/30/45.« less
Authors:
; ;  [1] ;  [1] ;  [2] ; ;  [1] ;  [1]
  1. Key Laboratory of Catalysis and Material Science of the State Ethnic Affairs Commission and Ministry of Education, Hubei Province, College of Chemistry and Material Science, South-Central University for Nationalities, Wuhan 430074 (China)
  2. (China)
Publication Date:
OSTI Identifier:
22341850
Resource Type:
Journal Article
Resource Relation:
Journal Name: Materials Research Bulletin; Journal Volume: 49; Other Information: Copyright (c) 2013 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
36 MATERIALS SCIENCE; 77 NANOSCIENCE AND NANOTECHNOLOGY; ELECTRON DIFFRACTION; IRRADIATION; NANOPARTICLES; NANOSTRUCTURES; OXIDATION; PLATINUM; PVP; REDUCING AGENTS; SOLVENTS; SYNTHESIS