Title: Europium doped lanthanum zirconate nanoparticles with high concentration quenching

Graphical abstract: - Highlights: • Eu:La{sub 2}Zr{sub 2}O{sub 7} nanoparticles were prepared facilely by a kinetically modified molten salt method. • High color purity and concentration quenching were achieved in these La{sub 2}Zr{sub 2}O{sub 7}:Eu nanoparticles. • Concentration quenching mechanism was discussed for Eu{sup 3+} in these Eu:La{sub 2}Zr{sub 2}O{sub 7} nanoparticles. - Abstract: A series of Eu{sup 3+} doped lanthanum zirconate (La{sub 2}Zr{sub 2}O{sub 7}) nanoparticles (NPs, 20 ± 5 nm in diameter) with cubic fluorite structure were facilely synthesized by a kinetically modified molten salt synthetic (MSS) process and characterized by X-ray diffraction (XRD), scanning electron microscope (SEM), transmission electron microscope (TEM) and photoluminescence spectra (PL). Under the excitation of 405 nm, intense red emission with high color purity can be observed in the Eu{sup 3+} doped La{sub 2}Zr{sub 2}O{sub 7} NPs. Moreover, the as-prepared Eu:La{sub 2}Zr{sub 2}O{sub 7} NPs possess high concentration quenching, which is as high as ∼32.5 mol% of europium dopants in the La{sub 2}Zr{sub 2}O{sub 7} host. The corresponding concentration quenching mechanism was discussed as well. Our results confirm that the kinetically modified MSS process is a promising approach for preparing rare earth (RE) ions doped A{sub 2}B{sub 2}O{sub 7} nanoparticles with uniform REmore » doping and high concentration quenching.« less
Authors:
; ; ;
Publication Date:
OSTI Identifier:
22341824
Resource Type:
Journal Article
Resource Relation:
Journal Name: Materials Research Bulletin; Journal Volume: 49; Other Information: Copyright (c) 2013 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
36 MATERIALS SCIENCE; DOPED MATERIALS; EUROPIUM; FLUORITE; LANTHANUM; MOLTEN SALTS; NANOPARTICLES; NANOSTRUCTURES; PHOTOLUMINESCENCE; SCANNING ELECTRON MICROSCOPY; SPECTRA; SYNTHESIS; TRANSMISSION ELECTRON MICROSCOPY; X-RAY DIFFRACTION; ZIRCONATES