Title: Electrochemical performances of co-substituted (La and Li) LiLa{sub x−y}Li{sub y}Ni{sub 1−x}O{sub 2} cathode materials for rechargeable lithium-ion batteries

Graphical abstract: - Highlights: • LiLa{sub x−y}Li{sub x}Ni{sub 1−x}O{sub 2} powders were prepared by a sol–gel method at 600 °C for 10 h. • LiLa{sub x−y}Li{sub x}Ni{sub 1−x}O{sub 2} powder materials had well defined layer structure, and no impurities. • LiLa{sub 0.10}Li{sub 0.10}Ni{sub 0.80}O{sub 2} crystallite size was reduced compared with those of LiNiO{sub 2}. • Li/LiPF{sub 6}/LiLa{sub x−y}Li{sub x}Ni{sub 1−x}O{sub 2} cells were of high charge/discharge capacity, with columbic efficiency at 25 °C and 45 °C. • LiLa{sub 0.10}Li{sub 0.10}Ni{sub 0.80}O{sub 2} good cyclic stability, rate capability and better 45 °C. - Abstract: Co-substituted LiLa{sub x−y}Li{sub y}Ni{sub 1−x}O{sub 2} cathode materials were synthesized by sol–gel method using aqueous solutions of metal nitrates and tartaric acid as chelating agent at 600 °C for 10 h. The structure and electrochemical properties of the synthesized materials were characterized by using XRD, SEM, EDAX, TEM, cyclic voltammetry, charge/discharge and electrochemical impedance spectroscopy. XRD studies revealed a well defined layer structure and a linear variation of lattice parameters with the addition of lanthanum and lithium confirmed phase pure compounds in a rhombohedral structure. TEM and SEM analysis shows that LiLa{sub 0.10}Li{sub 0.10}Ni{sub 0.80}O{sub 2} has smaller particle size and regular morphological structure with narrowmore » size distribution than those of LiNiO{sub 2}. Variations of dual mixing and hexagonal ordering with the substituted elements have enhanced the charge/discharge capacities at both room (25 °C) and elevated temperatures (45 °C), respectively. LiLa{sub 0.10}Li{sub 0.10}Ni{sub 0.80}O{sub 2} had high charge/discharge capacity, low irreversible capacity and better elevated temperature performance.« less
Authors:
;
Publication Date:
OSTI Identifier:
22341748
Resource Type:
Journal Article
Resource Relation:
Journal Name: Materials Research Bulletin; Journal Volume: 48; Journal Issue: 9; Other Information: Copyright (c) 2013 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
36 MATERIALS SCIENCE; AQUEOUS SOLUTIONS; CHELATING AGENTS; DISTRIBUTION; EFFICIENCY; LANTHANUM; LATTICE PARAMETERS; LAYERS; LITHIUM; LITHIUM ION BATTERIES; LITHIUM IONS; NITRATES; PARTICLE SIZE; SCANNING ELECTRON MICROSCOPY; SOL-GEL PROCESS; SPECTROSCOPY; TRANSMISSION ELECTRON MICROSCOPY; TRIGONAL LATTICES; VOLTAMETRY; X-RAY DIFFRACTION