Title: WO{sub 3} nanoplates, hierarchical flower-like assemblies and their photocatalytic properties

Graphical abstract: WO{sub 3} nanoplates, hierarchical flower-like assemblies and their visible light-driven photocatalytic properties for degradation of rhodamine B. - Highlights: • Preparation of monoclinic WO{sub 3} by a hydrothermal reaction of PbWO{sub 4} in the presence of HNO{sub 3}. • Single-crystalline WO{sub 3} nanoplates were formed when 4 M HNO{sub 3} solution was used. • WO{sub 3} flowers were assembled by nanoplates when 15 M HNO{sub 3} solution was used. • The products showed excellent visible light-driven photodegradation of rhodamine B. - Abstract: Monoclinic WO{sub 3} was prepared by a hydrothermal reaction of PbWO{sub 4} in the presence of HNO{sub 3}. WO{sub 3} rectangular nanoplates with a side length of 50–150 nm and a thickness of about 25 nm were obtained at 4 M HNO{sub 3} solution. And the single crystal nature was confirmed by the selected area electron diffraction. Whereas WO{sub 3} hierarchical flower-like assemblies with 3–5 μm in diameter were self-organized by nanoplates in the presence of 15 M HNO{sub 3} solution. Compared with commercial WO{sub 3} particles, our products showed an enhancement of photocatalytic properties for the degradation of rhodamine B under visible light irradiation.
Authors:
; ;
Publication Date:
OSTI Identifier:
22341716
Resource Type:
Journal Article
Resource Relation:
Journal Name: Materials Research Bulletin; Journal Volume: 48; Journal Issue: 8; Other Information: Copyright (c) 2013 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
36 MATERIALS SCIENCE; ELECTRON DIFFRACTION; ELECTRON MICROSCOPY; HYDROTHERMAL SYNTHESIS; IRRADIATION; LEAD TUNGSTATES; MONOCLINIC LATTICES; MONOCRYSTALS; NITRIC ACID; PARTICLES; PHOTOCATALYSIS; THICKNESS; TUNGSTEN OXIDES; X-RAY DIFFRACTION