Title: Electronic passivation of silicon surfaces by thin films of atomic layer deposited gallium oxide

This paper proposes the application of gallium oxide (Ga{sub 2}O{sub 3}) thin films to crystalline silicon solar cells. Effective passivation of n- and p-type crystalline silicon surfaces has been achieved by the application of very thin Ga{sub 2}O{sub 3} films prepared by atomic layer deposition using trimethylgallium (TMGa) and ozone (O{sub 3}) as the reactants. Surface recombination velocities as low as 6.1 cm/s have been recorded with films less than 4.5 nm thick. A range of deposition parameters has been explored, with growth rates of approximately 0.2 Å/cycle providing optimum passivation. The thermal activation energy for passivation of the Si-Ga{sub 2}O{sub 3} interface has been found to be approximately 0.5 eV. Depassivation of the interface was observed for prolonged annealing at increased temperatures. The activation energy for depassivation was measured to be 1.9 eV.
Authors:
;  [1]
  1. Research School of Engineering, Australian National University, Canberra 0200 (Australia)
Publication Date:
OSTI Identifier:
22311125
Resource Type:
Journal Article
Resource Relation:
Journal Name: Applied Physics Letters; Journal Volume: 105; Journal Issue: 3; Other Information: (c) 2014 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND SUPERFLUIDITY; ACTIVATION ENERGY; ANNEALING; CRYSTAL GROWTH; DEPOSITION; GALLIUM OXIDES; INTERFACES; LAYERS; PASSIVATION; RECOMBINATION; SILICON; SILICON SOLAR CELLS; SURFACES; THIN FILMS