Title: Graphene oxide hole transport layers for large area, high efficiency organic solar cells

Graphene oxide (GO) is becoming increasingly popular for organic electronic applications. We present large active area (0.64 cm{sup 2}), solution processable, poly[[9-(1-octylnonyl)-9H-carbazole-2,7-diyl]-2,5-thiophenediyl-2,1, 3-benzothiadiazole-4,7-diyl-2,5-thiophenediyl]:[6,6]-Phenyl C{sub 71} butyric acid methyl ester (PCDTBT:PC{sub 70}BM) organic photovoltaic (OPV) solar cells, incorporating GO hole transport layers (HTL). The power conversion efficiency (PCE) of ∼5% is the highest reported for OPV using this architecture. A comparative study of solution-processable devices has been undertaken to benchmark GO OPV performance with poly(3,4-ethylenedioxythiophene) poly(styrenesulfonate) (PEDOT:PSS) HTL devices, confirming the viability of GO devices, with comparable PCEs, suitable as high chemical and thermal stability replacements for PEDOT:PSS in OPV.
Authors:
; ; ; ; ; ;  [1]
  1. Advanced Technology Institute, University of Surrey, Guildford GU2 7XH (United Kingdom)
Publication Date:
OSTI Identifier:
22310914
Resource Type:
Journal Article
Resource Relation:
Journal Name: Applied Physics Letters; Journal Volume: 105; Journal Issue: 7; Other Information: (c) 2014 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND SUPERFLUIDITY; BENCHMARKS; CONVERSION; EFFICIENCY; GRAPHENE; HOLE MOBILITY; HOLES; LAYERS; ORGANIC SOLAR CELLS; OXIDES; PHOTOVOLTAIC EFFECT; STABILITY