Temperature of broadband anti-Stokes white emission in LiYbP{sub 4}O{sub 12}: Er nanocrystals
- Institute of Low Temperature and Structure Research, Polish Academy of Sciences, 50-422 Wrocław (Poland)
- Institute Light Matter (ILM), UMR5306 CNRS-University Lyon1, University of Lyon, 69622 Villeurbanne (France)
The up-conversion emission of LiYb{sub 0.99}Er{sub 0.01}P{sub 4}O{sub 12} nanocrystals was investigated in vacuum upon the focused beam of infrared laser excitation. The intense white broad band emission was observed above the threshold power of 800 mW. An increase of excitation power results in enhancement of temperature of emitting nanocrystals. The temperature of nanocrystals was determined following the thermally equilibrated f-f emission transitions of Er{sup 3+} ions. The highest measured temperature of white emission was determined to be about 900 K. It is concluded that the black body radiation is not responsible for the white broad band emission.
- OSTI ID:
- 22310677
- Journal Information:
- Applied Physics Letters, Vol. 105, Issue 17; Other Information: (c) 2014 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0003-6951
- Country of Publication:
- United States
- Language:
- English
Similar Records
Hydrothermal synthesis and luminescence properties of octahedral LiYbF{sub 4}: Er{sup 3+} microcrystals
White light generation via sequential stepwise absorption and energy-transfer frequency upconversion in Tm{sup 3+}/Er{sup 3+}-codoped glass
Visible and infrared luminescence properties of Er{sup 3+}-doped Y{sub 2}Ti{sub 2}O{sub 7} nanocrystals
Journal Article
·
Tue Feb 15 00:00:00 EST 2011
· Materials Research Bulletin
·
OSTI ID:22310677
+1 more
White light generation via sequential stepwise absorption and energy-transfer frequency upconversion in Tm{sup 3+}/Er{sup 3+}-codoped glass
Journal Article
·
Wed Nov 15 00:00:00 EST 2017
· Journal of Solid State Chemistry
·
OSTI ID:22310677
Visible and infrared luminescence properties of Er{sup 3+}-doped Y{sub 2}Ti{sub 2}O{sub 7} nanocrystals
Journal Article
·
Tue Mar 15 00:00:00 EDT 2011
· Journal of Solid State Chemistry
·
OSTI ID:22310677
+1 more