The thickness-dependent dynamic magnetic property of Co{sub 2}FeAl films grown by molecular beam epitaxy
- State Key Laboratory of Superlattices and Microstructures, Institute of Semiconductors, Chinese Academy of Sciences, P.O. Box 912, Beijing 100083 (China)
Co{sub 2}FeAl films with different thickness were prepared at different temperature by molecular beam epitaxy. Their dynamic magnetic property was studied by the time-resolved magneto-optical Kerr effect measurements. It is observed that the intrinsic damping factor of Co{sub 2}FeAl for [100] orientation is not related to the film's thickness and magnetic anisotropy as well as temperature at high-field regime, but increases with structural disorder of Co{sub 2}FeAl. The dominant contribution from the inhomogeneous magnetic anisotropy is revealed to be responsible for the observed extremely nonlinear and drastic field-dependent damping factors at low-field regime.
- OSTI ID:
- 22310660
- Journal Information:
- Applied Physics Letters, Vol. 105, Issue 17; Other Information: (c) 2014 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0003-6951
- Country of Publication:
- United States
- Language:
- English
Similar Records
The in-plane anisotropic magnetic damping of ultrathin epitaxial Co{sub 2}FeAl film
Temperature dependent magnetic anisotropy of epitaxial Co{sub 2}FeAl films grown on GaAs
Magnetic and Gilbert damping properties of L{sub 21}-Co{sub 2}FeAl film grown by molecular beam epitaxy
Journal Article
·
Sat Aug 15 00:00:00 EDT 2015
· AIP Advances
·
OSTI ID:22310660
+2 more
Temperature dependent magnetic anisotropy of epitaxial Co{sub 2}FeAl films grown on GaAs
Journal Article
·
Sat Mar 07 00:00:00 EST 2015
· Journal of Applied Physics
·
OSTI ID:22310660
+1 more
Magnetic and Gilbert damping properties of L{sub 21}-Co{sub 2}FeAl film grown by molecular beam epitaxy
Journal Article
·
Mon Oct 07 00:00:00 EDT 2013
· Applied Physics Letters
·
OSTI ID:22310660
+3 more