Uniformly dispersed CdS nanoparticles sensitized TiO{sub 2} nanotube arrays with enhanced visible-light photocatalytic activity and stability
- School of Materials Science and Engineering, Hefei University of Technology, Hefei 230009 (China)
- School of Materials Science and Engineering, Nanyang Technological University, 50 Nanyang Avenue 639798 (Singapore)
In this study, TiO{sub 2} nanotube arrays (TiO{sub 2}-NTs) with various intertube spaces were fabricated in the electrolyte with different water contents and the CdS nanoparticles (CdS NPs) were further deposited onto the TiO{sub 2}-NTs as a sensitizer via a sequential chemical bath deposition (S-CBD) method. The FE-SEM, TEM, XRD and XPS results demonstrated that the CdS NPs were uniformly deposited onto the surface of TiO{sub 2}-NTs. It was found that higher water content in electrolyte was in favor of large intertube space and pore size and the uniform deposition of CdS NPs. The photocatalytic degradation of methyl orange was tested with the as-prepared CdS/TiO{sub 2}-NTs under visible light (λ>400 nm). It was found that the photodegradation rate reached as high as 96.7% under visible irradiation for 180 min. In addition, a reasonable degradation rate of 75.8% was achieved even after 5 cycles, suggesting a good photocatalytic stability of the as-prepared CdS/TiO{sub 2}-NTs. - Graphical abstract: The whole sheet of CdS NPs sensitized TiO{sub 2}-NTs with the Ti subtract was used for degradation of methyl orange under visible light (λ>400 nm) on a XPA-7 photochemical reactor. - Highlights: • Intertube space, pore size were controlled by changing water content in electrolyte. • CdS nanoparticles were uniformly deposited onto the surface of TiO{sub 2} nanotubes. • The catalyst with Ti substrate used as a whole was very convenient for recycling. • Visible-light photocatalytic activity and stability were highly enhanced.
- OSTI ID:
- 22309062
- Journal Information:
- Journal of Solid State Chemistry, Vol. 208; Other Information: Copyright (c) 2013 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0022-4596
- Country of Publication:
- United States
- Language:
- English
Similar Records
Fabrication and photocatalytic activity of high-efficiency visible-light-responsive photocatalyst ZnTe/TiO{sub 2} nanotube arrays
Improving the visible light photocatalytic activity of TiO{sub 2} nanotubes upon decoration with Sb{sub 2}S{sub 3} microcrystalline