Title: Synthesis, structural and magnetic characterisation of the fluorinated compound 15R-BaFeO{sub 2}F

The compounds 15R-BaFeO{sub 2}F and 15R-BaFeO{sub 2.27}F{sub 0.5} have been synthesised by the low temperature fluorination of 15R-BaFeO{sub 3−d}F{sub 0.2} using polyvinylidenedifluoride (PVDF) as a fluorination agent. The materials have been structurally characterised by Rietveld analysis of the X-ray- and HRPD-powder neutron diffraction data. A detailed analysis of bond valence sums suggests that the oxide and fluoride ions order on the different anion sites. A reinvestigation of our recently published structure (Clemens et al., 2013) [34] of 6H-BaFeO{sub 2}F is also reported and incorporation of fluoride in h-type layers is also confirmed in this compound. The magnetic moments for 15R-BaFeO{sub 2}F and 15R-BaFeO{sub 2.25}F{sub 0.5} align in the a/b-plane with antiferromagnetic alignment of the moments between adjacent layers, and are flipped by 90° as compared to the precursor compound. 15R-BaFeO{sub 2}F exhibits very robust antiferromagnetism with a Néel temperature between 300 and 400 °C. - Graphical abstract: The crystal and magnetic structure of the perovskite phase 15R-BaFeO{sub 2}F. - Highlights: • 15R-BaFeO{sub 2}F and 15R-BaFeO{sub 2.27}F{sub 0.5}were prepared via low temperature fluorination using PVDF. • A structural investigation of the compounds BaFeO{sub 2}F is presented in detail. • This analysis suggests ordering of O{sup 2−} and F{sup −} anions betweenmore » different layers. • 15R-BaFeO{sub 2}F shows antiferromagnetic ordering at 300 K with T{sub N} ∼300–400 °C. • The magnetic moments align in the a/b-plane.« less
Authors:
 [1] ;  [1] ;  [2] ;  [1] ;  [3] ;  [1]
  1. School of Chemistry, The University of Birmingham, Birmingham B15 2TT (United Kingdom)
  2. Anorganische Festkörperchemie, Universität des Saarlandes, Am Markt, Zeile 3, 66125 Saarbrücken (Germany)
  3. ISIS Facility, Rutherford Appleton Laboratory, Harwell Oxford, Didcot OX11 0QX (United Kingdom)
Publication Date:
OSTI Identifier:
22309040
Resource Type:
Journal Article
Resource Relation:
Journal Name: Journal of Solid State Chemistry; Journal Volume: 203; Other Information: Copyright (c) 2013 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
37 INORGANIC, ORGANIC, PHYSICAL AND ANALYTICAL CHEMISTRY; ANIONS; ANTIFERROMAGNETISM; CRYSTALS; FLUORIDES; FLUORINATION; LAYERS; MAGNETIC MOMENTS; NEUTRON DIFFRACTION; ORGANIC FLUORINE COMPOUNDS; OXIDES; PEROVSKITE; POLYVINYLS; SYNTHESIS; X RADIATION