Presence of a monoclinic (Pm) phase in the morphotropic phase boundary region of multiferroic (1 − x)Bi(Ni{sub 1/2}Ti{sub 1/2})O{sub 3}-xPbTiO{sub 3} solid solution: A Rietveld study

Journal Article · Mon Jul 28 00:00:00 EDT 2014 · Journal of Applied Physics

DOI:https://doi.org/10.1063/1.4891106· OSTI ID:22308544

Pandey, Rishikesh

We present here the results of structural studies on multiferroic (1 − x)Bi(Ni{sub 1/2}Ti{sub 1/2})O{sub 3}-xPbTiO{sub 3} solid solution using Rietveld analysis on powder x-ray diffraction data in the composition range 0.35 ≤ x ≤ 0.55. The stability region of various crystallographic phases at room temperature for (1 − x)Bi(Ni{sub 1/2}Ti{sub 1/2})O{sub 3}-xPbTiO{sub 3} is determined precisely. Structural transformation from pseudo-cubic (x ≤ 0.40) to tetragonal (x ≥ 0.50) phase is observed via phase coexistence region demarcating the morphotropic phase boundary. The morphotropic phase boundary region consists of coexisting tetragonal and monoclinic structures with space group P4mm and Pm, respectively, stable in composition range 0.41 ≤ x ≤ 0.49 as confirmed by Rietveld analysis. The results of Rietveld analysis completely rule out the coexistence of rhombohedral and tetragonal phases in the morphotropic phase boundary region reported by earlier workers. A comparison between the bond lengths for “B-site cations-oxygen anions” obtained after Rietveld refinement, with the bond length calculated using Shannon-Prewitt ionic radii, reveals the ionic nature of B-O (Ni/Ti-O) bonds for the cubic phase and partial covalent character for the other crystallographic phases.

• OSTI ID: 22308544
• Journal Information: Journal of Applied Physics, Vol. 116, Issue 4; Other Information: (c) 2014 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0021-8979
• Country of Publication: United States
• Language: English

Related Subjects

75 CONDENSED MATTER PHYSICS
SUPERCONDUCTIVITY AND SUPERFLUIDITY
BISMUTH COMPOUNDS
BOND LENGTHS
COVALENCE
CRYSTALLOGRAPHY
LEAD COMPOUNDS
MONOCLINIC LATTICES
NICKEL COMPOUNDS
OXYGEN
OXYGEN COMPOUNDS
POWDERS
SOLID SOLUTIONS
SPACE GROUPS
STABILITY
TEMPERATURE RANGE 0273-0400 K
TETRAGONAL LATTICES
TITANATES
TITANIUM COMPOUNDS
TRANSFORMATIONS
TRIGONAL LATTICES
X-RAY DIFFRACTION