Title: Effect of annealing process on the phase formation in poly(vinylidene fluoride) thin films

This work reports the initial study on the effect of annealing process on the crystalline phase of poly(vinylidene fluoride) (PVDF) thin film. PVDF powder was dissolved in N,N-dimethylformamide before spin-coated onto a glass substrate to form a film. The films were annealed at 30°C, 90°C and 110°C for 5 hrs. The crystalline phase of the powder PVDF as received was investigated by using XRD and FTIR techniques. Moreover, the crystalline phases of thin films after annealing were investigated by using the same techniques. XRD analysis showed that in powder form PVDF exists in α-phase. Each annealed PVDF thin films exhibited identical formation of three-phases material namely γ (as major phase) while α and β phases as the minor phases. The FTIR analysis showed that the powder form of PVDF exists in α and β phases. FTIR measurement further confirmed the XRD results implying that the annealing process has no significant effect on the phase formation in PVDF films.
Authors:
; ; ;  [1]
  1. School of Applied Physics, Faculty of Science and Technology, Universiti Kebangsaan Malaysia, 43600 UKM Bangi, Selangor (Malaysia)
Publication Date:
OSTI Identifier:
22308311
Resource Type:
Journal Article
Resource Relation:
Journal Name: AIP Conference Proceedings; Journal Volume: 1614; Journal Issue: 1; Conference: 2014 UKM FST postgraduate colloquium, Selangor (Malaysia), 9-11 Apr 2014; Other Information: (c) 2014 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
36 MATERIALS SCIENCE; ANNEALING; FLUORINATED ALIPHATIC HYDROCARBONS; FOURIER TRANSFORMATION; INFRARED SPECTRA; POLYVINYLS; POWDERS; SUBSTRATES; THIN FILMS; X-RAY DIFFRACTION