Title: Substitution behavior of x(Na{sub 0.5}K{sub 0.5})NbO{sub 3}-(1 − x)BaTiO{sub 3} ceramics for multilayer ceramic capacitors by a near edge x-ray absorption fine structure analysis

The doping effect of (Na{sub 0.5}K{sub 0.5})NbO{sub 3} (NKN) as alternatives for rare-earth elements on the electrical properties of BaTiO{sub 3} has been investigated, in terms of their substitution behavior. The dielectric constant of a specimen with x = 0.05 was about 79% higher than that of pure BaTiO{sub 3}, and the temperature coefficient of capacitance was satisfied by the X7R specification. The specimen with x = 0.05 showed the lowest tetragonality among the four compositions and had a fine grain size of <2 μm. Although the addition of NKN decreased the specimen's tetragonality, the electrical properties were enhanced by the formation of defect dipoles and conduction electrons, which resulted from an acceptor and donor substitution behavior. Through O K-edge near edge x-ray absorption fine structure spectroscopy, the practical substitution behavior was defined by the change in Ti 3d orbital states. The energy separation of the Ti 3d orbitals was more apparent with the specimen of x = 0.05, which is related to the donor level from the donor substitution of Nb{sup 5+} ion for Ti-sites. Therefore, the simultaneous substitution of Na{sup +}/K{sup +} and Nb{sup 5+} ions into BaTiO{sub 3} can improve dielectric properties, based on the charge-transfer process.
Authors:
; ;  [1]
  1. School of Materials Science and Engineering, Pusan National University, Busan 609-735 (Korea, Republic of)
Publication Date:
OSTI Identifier:
22303900
Resource Type:
Journal Article
Resource Relation:
Journal Name: Applied Physics Letters; Journal Volume: 104; Journal Issue: 26; Other Information: (c) 2014 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND SUPERFLUIDITY; ABSORPTION; ABSORPTION SPECTROSCOPY; BARIUM COMPOUNDS; CAPACITORS; CERAMICS; CRYSTAL DEFECTS; DIPOLES; FINE STRUCTURE; GRAIN SIZE; LAYERS; NIOBATES; PERMITTIVITY; POTASSIUM COMPOUNDS; RARE EARTHS; SODIUM COMPOUNDS; TEMPERATURE COEFFICIENT; TITANATES; X RADIATION; X-RAY SPECTROSCOPY