Title: Low-voltage organic field-effect transistors based on novel high-κ organometallic lanthanide complex for gate insulating materials

A novel high-κ organometallic lanthanide complex, Eu(tta){sub 3}L (tta=2-thenoyltrifluoroacetonate, L = 4,5-pinene bipyridine), is used as gate insulating material to fabricate low-voltage pentacene field-effect transistors (FETs). The optimized gate insulator exhibits the excellent properties such as low leakage current density, low surface roughness, and high dielectric constant. When operated under a low voltage of −5 V, the pentacene FET devices show the attractive electrical performance, e.g. carrier mobility (μ{sub FET}) of 0.17 cm{sup 2} V{sup −1} s{sup −1}, threshold voltage (V{sub th}) of −0.9 V, on/off current ratio of 5 × 10{sup 3}, and subthreshold slope (SS) of 1.0 V dec{sup −1}, which is much better than that of devices obtained on conventional 300 nm SiO{sub 2} substrate (0.13 cm{sup 2} V{sup −1} s{sup −1}, −7.3 V and 3.1 V dec{sup −1} for μ{sub FET}, V{sub th} and SS value when operated at −30 V). These results indicate that this kind of high-κ organometallic lanthanide complex becomes a promising candidate as gate insulator for low-voltage organic FETs.
Authors:
; ; ; ; ;  [1] ; ; ;  [2]
  1. Key Laboratory of Mesoscopic Chemistry of MOE, Jiangsu Provincial Lab for Nanotechnology, School of Chemistry and Chemical Engineering, Nanjing University, Nanjing 210093, China. High-Tech Research Institute of Nanjing University (Suzhou), Suzhou 215123 (China)
  2. School of Electronic Science and Engineering and Jiangsu Provincial Key Laboratory of Photonic and Electronic Materials, Nanjing University, Nanjing 210093 (China)
Publication Date:
OSTI Identifier:
22299761
Resource Type:
Journal Article
Resource Relation:
Journal Name: AIP Advances; Journal Volume: 4; Journal Issue: 8; Other Information: (c) 2014 Author(s); Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
36 MATERIALS SCIENCE; CARRIER MOBILITY; ELECTRIC POTENTIAL; FIELD EFFECT TRANSISTORS; LEAKAGE CURRENT; ORGANOMETALLIC COMPOUNDS; PERMITTIVITY; RARE EARTH COMPLEXES; SILICA; SILICON OXIDES; SUBSTRATES; SURFACES