Title: A detailed examination of the growth of CdSe thin films through structural and optical characterization

Highlights: ► Urbach tail width decreases by about 200 meV with the film thickness. ► A coefficient of strain of around 3 × 10{sup −3} along [0 0 2] axis was predicted. ► Compressive strain gives rise to about 11 meV red shift in the band gap energy. ► A relative shift of about 2 cm{sup −1} of LO{sub 1} phonon mode in Raman spectra was observed between different thickness films. - Abstract: Different thickness CdSe thin films were grown on glass substrates by physical vapor deposition and characterized by optical and structural investigations. Urbach energy related to the width of the optical absorption tail decreases from 430 meV for a film thickness of 50 nm to 200 meV for 450 nm. The film thickness dependent grain sizes were estimated by using effective mass model under quantum size effect from the shift of around 500 meV in the asymptotic absorption edge. The X-ray diffraction (XRD) pattern is consistent with CdSe hexagonal crystal structure which indicates crystal growth mode along c axis. XRD peaks broaden and shift depending on film thicknesses which are presumably due to strain and size effect. We observe both blue and red shift depending on thickness inmore » Longitudinal Optical phonon frequency in Raman spectra with respect to that of the source CdSe powder which could also be due to strain on thin films and/or finite crystallite size. In this work we combine the results of optical absorption, Raman and XRD spectroscopies to study the evolution of grain size, strain and structural disorder depending on film thickness.« less
Authors:
 [1] ; ;  [1]
  1. Yıldız Technical University, Faculty of Science and Letters, Department of Physics, 34220 Davutpasa-Esenler, Istanbul (Turkey)
Publication Date:
OSTI Identifier:
22290454
Resource Type:
Journal Article
Resource Relation:
Journal Name: Materials Research Bulletin; Journal Volume: 48; Journal Issue: 7; Other Information: Copyright (c) 2013 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
36 MATERIALS SCIENCE; ABSORPTION; CADMIUM SELENIDES; CRYSTAL STRUCTURE; EFFECTIVE MASS; GRAIN SIZE; OPTICAL PROPERTIES; PHONONS; PHYSICAL VAPOR DEPOSITION; RAMAN SPECTRA; RED SHIFT; STRAINS; THICKNESS; THIN FILMS; X-RAY DIFFRACTION