Title: Microstructure and mechanical properties of diffusion bonded W/steel joint using V/Ni composite interlayer

Diffusion bonding between W and steel using V/Ni composite interlayer was carried out in vacuum at 1050 °C and 10 MPa for 1 h. The microstructural examination and mechanical property evaluation of the joints show that the bonding of W to steel was successful. No intermetallic compound was observed at the steel/Ni and V/W interfaces for the joints bonded. The electron probe microanalysis and X-ray diffraction analysis revealed that Ni{sub 3}V, Ni{sub 2}V, Ni{sub 2}V{sub 3} and NiV{sub 3} were formed at the Ni/V interface. The tensile strength of about 362 MPa was obtained for as-bonded W/steel joint and the failure occurred at W near the V/W interface. The nano-indentation test across the joining interfaces demonstrated the effect of solid solution strengthening and intermetallic compound formation in the diffusion zone. - Highlights: • Diffusion bonding of W to steel was realized using V/Ni composite interlayer. • The interfacial microstructure of the joint was clarified. • Several V–Ni intermetallic compounds were formed in the interface region. • The application of V/Ni composite interlayer improved the joining quality.
Authors:
; ; ; ; ;
Publication Date:
OSTI Identifier:
22288705
Resource Type:
Journal Article
Resource Relation:
Journal Name: Materials Characterization; Journal Volume: 86; Other Information: Copyright (c) 2013 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
36 MATERIALS SCIENCE; BONDING; ELECTRON MICROPROBE ANALYSIS; INTERMETALLIC COMPOUNDS; MICROSTRUCTURE; PRESSURE RANGE MEGA PA 100-1000; SOLID SOLUTIONS; STEELS; TENSILE PROPERTIES; X-RAY DIFFRACTION