Title: Refinement of Mg{sub 2}Si reinforcement in a commercial Al–20%Mg{sub 2}Si in-situ composite with bismuth, antimony and strontium

Refinement by addition elements of Al–Mg{sub 2}Si alloys is known to result in a change of primary Mg{sub 2}Si morphology. In this paper, the effects of Bi, Sb and Sr on the characteristic parameters of Al–20%Mg{sub 2}Si in-situ composite have been investigated by computer aided cooling curve thermal analysis and microstructural inspection. Size, density and aspect ratio measurements showed that additions of 0.4 wt.% Bi, 0.8 wt.% Sb and 0.01 wt.% Sr refined the Mg{sub 2}Si reinforcement. Exceeding these concentrations, however, resulted in coarsening of Mg{sub 2}Si particles with no change in the morphology. The results also showed that addition elements caused a decrease in the nucleation and growth temperatures of Mg{sub 2}Si particles. The refining effect of Bi, Sb and Sr is likely to be related to the effect of oxide bifilms suspended in the composite melt as favored nucleation substrates for Mg{sub 2}Si particles. - Highlight: • 0.4 wt.%, 0.8 wt.% and 0.01 wt.% is the optimum content for Bi, Sb and Sr addition. • Exceeding optimum concentration resulted in the coarsening of reinforcements. • Nucleation and growth temperatures decrease with addition of Bi, Sb and Sr. • The refining effect of Bi, Sb and Sr is likelymore » to be related to the oxide bifilms.« less
Authors:
; ; ; ;
Publication Date:
OSTI Identifier:
22288693
Resource Type:
Journal Article
Resource Relation:
Journal Name: Materials Characterization; Journal Volume: 86; Other Information: Copyright (c) 2013 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
36 MATERIALS SCIENCE; ALLOYS; ANTIMONY; ASPECT RATIO; BISMUTH; MAGNESIUM SILICIDES; MICROSTRUCTURE; OXIDES; STRONTIUM; THERMAL ANALYSIS