Title: Nanocrystalline Cs{sub x}WO{sub 3} particles: Effects of N{sub 2} annealing on microstructure and near-infrared shielding characteristics

In order to further improve the near-infrared shielding properties of cesium tungsten bronze (Cs{sub x}WO{sub 3}) for solar filter applications, Cs{sub x}WO{sub 3} particles were prepared by solvothermal reaction method and the effects of nitrogen annealing on the microstructure and near-infrared shielding properties of Cs{sub x}WO{sub 3} were investigated. The obtained Cs{sub x}WO{sub 3} samples were characterized by X-ray diffraction, scanning electron microscopy, transmission electron microscopy, X-ray photoelectron spectroscopy and spectrophotometer. The results indicate that nanosheet-like Cs{sub x}WO{sub 3} particles with hexagonal structure began to transform into nanorods after annealed at temperature higher than 600 °C. The near-infrared shielding properties of Cs{sub x}WO{sub 3} particles could be further improved by N{sub 2} annealing at 500–700 °C. Particularly, the 500 °C-annealed Cs{sub x}WO{sub 3} samples in the N{sub 2} atmosphere showed best near-infrared shielding properties. It was suggested that the excellent near-infrared shielding ability of the 500 °C-annealed Cs{sub x}WO{sub 3} samples is correlated with its minimum O/W atomic ratio and most oxygen vacancies. Highlights: • N{sub 2} annealing could further improve the near-infrared (NIR) shielding of Cs{sub x}WO{sub 3}. • Effects of N{sub 2} annealing on microstructure and NIR shielding of Cs{sub x}WO{sub 3} were studied. • The 500 °C-N{submore » 2}-annealed Cs{sub x}WO{sub 3} exhibited minimum O/W ratio and most oxygen vacancies. • The 500 °C-N{sub 2}-annealed Cs{sub x}WO{sub 3} particles exhibited best NIR shielding properties.« less
Authors:
 [1] ;  [2] ; ; ;  [1] ; ;  [3]
  1. School of Textile and Material Engineering, Dalian Polytechnic University, Dalian 116034 (China)
  2. (Japan)
  3. Institute of Multidisciplinary Research for Advanced Material, Tohoku University, Sendai, 980-8577,Japan (Japan)
Publication Date:
OSTI Identifier:
22288674
Resource Type:
Journal Article
Resource Relation:
Journal Name: Materials Characterization; Journal Volume: 84; Other Information: Copyright (c) 2013 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
36 MATERIALS SCIENCE; ANNEALING; CESIUM; CRYSTALS; MICROSTRUCTURE; NANOSTRUCTURES; NITROGEN; PARTICLES; SCANNING ELECTRON MICROSCOPY; SHIELDING; SPECTROPHOTOMETERS; SYNTHESIS; TRANSMISSION ELECTRON MICROSCOPY; TUNGSTEN BRONZE; VACANCIES; X-RAY DIFFRACTION; X-RAY PHOTOELECTRON SPECTROSCOPY