Title: Effect of anionic surfactant concentration on the variable range hopping conduction in polypyrrole nanoparticles

The mechanism of charge transport in polypyrrole (PPy) nanoparticles prepared with different concentrations (5 to 30 mM) of anionic surfactant (sodium dodecyl sulfate) is reported. Transmission electron microscopy technique confirms the formation of PPy nanoparticles of sizes ∼52 to 28 nm under surfactant directed approach. The room temperature electrical conductivity of the prepared nanoparticles found to increase from 3 to 22 S/cm with surfactant concentration. The temperature dependent activation energy rules out the possibility of band conduction mechanism in the prepared PPy nanoparticles and thus the synthesized nanoparticles are analyzed under variable range hopping (VRH) model for conduction mechanism. The PPy nanoparticles, reduced with liquid ammonia, hold 3D VRH conduction mechanism for the charge transport. However, in the doped samples, some deviation from 3D VRH conduction behavior at higher temperatures (>150 K) has been observed. This may be attributed to the presence of anionic surfactant in these samples. The doping of anionic surfactant causes rise in conducting islands, which may lead to the change in the shape/distribution of density of states governed by Gaussian or exponential type near Fermi level.
Authors:
;  [1]
  1. Department of Physics and Astrophysics, University of Delhi, Delhi-110007 (India)
Publication Date:
OSTI Identifier:
22275611
Resource Type:
Journal Article
Resource Relation:
Journal Name: Journal of Applied Physics; Journal Volume: 115; Journal Issue: 4; Other Information: (c) 2014 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND SUPERFLUIDITY; 77 NANOSCIENCE AND NANOTECHNOLOGY; ACTIVATION ENERGY; AMMONIA; CHARGE TRANSPORT; CONCENTRATION RATIO; DOPED MATERIALS; ELECTRIC CONDUCTIVITY; FERMI LEVEL; NANOSTRUCTURES; ORGANIC POLYMERS; PARTICLES; SODIUM COMPOUNDS; SULFATES; SURFACTANTS; TEMPERATURE DEPENDENCE; TRANSMISSION ELECTRON MICROSCOPY