Substitution studies of Mn and Fe in Ln{sub 6}W{sub 4}Al{sub 43} (Ln=Gd, Yb) and the structure of Yb{sub 6}Ti{sub 4}Al{sub 43}
- Department of Chemistry, Louisiana State University, Baton Rouge, LA 70803 (United States)
- Department of Physics and Astronomy, Louisiana State University, Baton Rouge, LA 70803 (United States)
The synthesis and characterization of Mn- and Fe-substituted Ln{sub 6}W{sub 4}Al{sub 43} (Ln=Gd, Yb) and Yb{sub 6}Ti{sub 4}Al{sub 43} are reported. The compounds adopt the Ho{sub 6}Mo{sub 4}Al{sub 43} structure type with lattice parameters of a∼11 Å and c∼17.8 Å with structural site preferences for Mn and Fe. The magnetization of Yb{sub 6}W{sub 4}Al{sub 43} is sensitive to Mn and Fe doping, which is evident by an increase in the field dependent magnetization. Gd{sub 6}W{sub 4}Al{sub 43}, Gd{sub 6}W{sub 4}Al{sub 42.31(11)}Mn{sub 0.69(11)}, and Gd{sub 6}W{sub 4}Al{sub 41.69(12)}Fe{sub 1.30(12)} order antiferromagnetically in the ab- and c-directions at 15, 14, and 13 K, respectively, with positive Weiss constants, suggesting the presence of ferromagnetic exchange interactions. Anisotropic magnetization data of Gd{sub 6}W{sub 4}Al{sub 43−y}T{sub y} (T=Mn, Fe) analogs are discussed. - Graphical abstract: The magnetic susceptibility of Ln{sub 6}W{sub 4−x}Al{sub 43−y}T{sub x+y} (Ln = Gd, Yb; T= Mn, Fe). Display Omitted - Highlights: • Single crystals of Ln{sub 6}W{sub 4−x}Al{sub 43−y}T{sub x+y} were grown with Al-flux. • Anisotropic magnetic behavior were determined on single crystals. • Gd{sub 6}W{sub 4−x}Al{sub 43−y}T{sub x+y} (T=Mn, Fe) analogs order antiferromagnetically.
- OSTI ID:
- 22274226
- Journal Information:
- Journal of Solid State Chemistry, Vol. 210, Issue 1; Other Information: Copyright (c) 2013 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0022-4596
- Country of Publication:
- United States
- Language:
- English
Similar Records
Crystal growth and magnetic properties of Ln-Mn-Al (Ln=Gd, Yb) compounds of the CaCr{sub 2}Al{sub 10} and ThMn{sub 12} structure types
Crystal growth and magnetic behavior of R{sub 6}T{sub 13-x}Al{sub x}M{sub y} phases (R=La, Nd; T=Mn, Fe; M=main group) grown from lanthanide-rich eutectic fluxes