Title: Controlled release of ibuprofen by meso–macroporous silica

Structured meso–macroporous silica was successfully synthesized from an O/W emulsion using decane as a dispersed phase. Sodium silicate solution, which acts as a silica source and a poly(ethylene oxide)–poly(propylene oxide)–poly(ethylene oxide) (EO{sub 19}PO{sub 39}EO{sub 19}) denoted as P84 was used in order to stabilize the emulsion and as a mesopore template. The materials obtained were characterized through transmission electron microscopy (TEM), scanning electron microscopy (SEM), small-angle X-ray diffraction scattering (SAXS) and nitrogen adsorption–desorption isotherms. Ibuprofen (IBU) was selected as the model drug and loaded into ordered meso–macroporous materials. The effect of the materials’ properties on IBU drug loading and release was studied. The results showed that the loading of IBU increases as the macropore presence in the material is increased. The IBU adsorption process followed the Langmuir adsorption isotherm. A two-step release process, consisting of an initial fast release and then a slower release was observed. Macropores enhanced the adsorption capacity of the material; this was probably due to the fact that they allowed the drug to access internal pores. When only mesopores were present, ibuprofen was probably adsorbed on the mesopores close to the surface. Moreover, the more macropore present in the material, the slower the release behaviour observed,more » as the ibuprofen adsorbed in the internal pores had to diffuse along the macropore channels up to the surface of the material. The material obtained from a highly concentrated emulsion was functionalized with amino groups using two methods, the post-grafting mechanism and the co-condensation mechanism. Both routes improve IBU adsorption in the material and show good behaviour as a controlled drug delivery system. - Graphical abstract: Ibuprofen release profiles for the materials obtained from samples P84{sub m}eso (black diamonds), P84{sub 2}0% (white squares), P84{sub 5}0% (black triangles), P84{sub 7}5% (white diamonds), P84{sub 7}5% functionalized by grafting (black squares) and P84{sub 7}5% functionalized by co-condensation method (white triangles). Display Omitted - Highlights: • Ordered meso–macroporous material is used as a controlled delivery system for ibuprofen. • Incorporation of macropores in mesoporous silica improves ibuprofen adsorption. • Meso–macroporous structures provide a lower delivery than mesoporous silica. • APTES functionalization in meso–macroporous materials improves ibuprofen adsorption and delivery behaviour.« less
Authors:
; ; ; ;
Publication Date:
OSTI Identifier:
22274222
Resource Type:
Journal Article
Resource Relation:
Journal Name: Journal of Solid State Chemistry; Journal Volume: 210; Journal Issue: 1; Other Information: Copyright (c) 2013 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
37 INORGANIC, ORGANIC, PHYSICAL AND ANALYTICAL CHEMISTRY; 77 NANOSCIENCE AND NANOTECHNOLOGY; ADSORPTION; ADSORPTION ISOTHERMS; DECANE; EMULSIONS; NANOSTRUCTURES; OXIDES; POLYETHYLENE GLYCOLS; PROPYLENE; SCANNING ELECTRON MICROSCOPY; SILICA; SMALL ANGLE SCATTERING; SODIUM SILICATES; SURFACES; TRANSMISSION ELECTRON MICROSCOPY; X-RAY DIFFRACTION