Title: Phase equilibria in the quasi-ternary system Ag{sub 2}Se–Ga{sub 2}Se{sub 3}–In{sub 2}Se{sub 3} and physical properties of (Ga{sub 0.6}In{sub 0.4}){sub 2}Se{sub 3}, (Ga{sub 0.594}In{sub 0.396}Er{sub 0.01}){sub 2}Se{sub 3} single crystals

The quasi-ternary system Ag{sub 2}Se–Ga{sub 2}Se{sub 3}–In{sub 2}Se{sub 3} was investigated by differential thermal, X-ray phase, X-ray structure, microstructure analysis and microhardness measurements. Five quasi-binary phase diagrams, six polythermal sections, isothermal section at 820 K and the liquidus surface projection were constructed. The character and temperature of the invariant processes were determined. The specific resistance of the single crystals (Ga{sub 0.6}In{sub 0.4}){sub 2}Se{sub 3}, (Ga{sub 0.594}In{sub 0.396}Er{sub 0.01}){sub 2}Se{sub 3} was measured, 7.5×10{sup 5} and 3.15×10{sup 5} Ω m, respectively, optical absorption spectra in the 600–1050 nm range were recorded at room temperature, and the band gap energy was estimated which is 1.95±0. 01 eV for both samples. - Graphical abstract: The article reports for the first time the investigated liquidus surface projection of the Ag{sub 2}Se–Ga{sub 2}Se{sub 3}–In{sub 2}Se{sub 3} system and isothermal section at 820 K of the system. Five phase diagrams, six polythermal sections, isothermal section at 820 K and the liquidus surface projection were built at the first time. The existence of the large region of the solid solutions based on AgIn{sub 5}Se{sub 8}, Ga{sub 2}Se{sub 3} and AgGa{sub 1−x}In{sub x}Se{sub 2} was investigated. The existence of two ternary phases was established in the Ga{sub 2}Se{submore » 3}–In{sub 2}Se{sub 3} system. Two single crystals (Ga{sub 0.6}In{sub 0.4}){sub 2}Se{sub 3}, (Ga{sub 0.594}In{sub 0.396}Er{sub 0.01}){sub 2}Se{sub 3} were grown and some of optical properties of them were studied at first time. Display Omitted - Highlights: • Liquidus surface projection was built for Ag{sub 2}Se–Ga{sub 2}Se{sub 3}–In{sub 2}Se{sub 3} system. • Solid solution ranges of AgIn{sub 5}Se{sub 8}, Ga{sub 2}Se{sub 3} and AgGa{sub 1−x}In{sub x}Se{sub 2} were investigated. • Two single crystals (Ga{sub 0.6}In{sub 0.4}){sub 2}Se{sub 3}, (Ga{sub 0.594}In{sub 0.396}Er{sub 0.01}){sub 2}Se{sub 3} were grown. • Some optical properties of these single crystals were studied.« less
Authors:
 [1] ; ;  [1] ;  [2]
  1. Department of Inorganic and Physical Chemistry, Eastern European National University, Voli Ave 13, Lutsk 43025 (Ukraine)
  2. Department of General Physics, Eastern European National University, Voli Ave 13, Lutsk 43025 (Ukraine)
Publication Date:
OSTI Identifier:
22274200
Resource Type:
Journal Article
Resource Relation:
Journal Name: Journal of Solid State Chemistry; Journal Volume: 210; Journal Issue: 1; Other Information: Copyright (c) 2013 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
37 INORGANIC, ORGANIC, PHYSICAL AND ANALYTICAL CHEMISTRY; 36 MATERIALS SCIENCE; ABSORPTION SPECTRA; GALLIUM SELENIDES; MICROHARDNESS; MICROSTRUCTURE; MONOCRYSTALS; OPTICAL PROPERTIES; PHASE DIAGRAMS; SOLID SOLUTIONS; SURFACES; THERMAL ANALYSIS; X RADIATION; X-RAY DIFFRACTION