Title: Crystal structures and magnetic properties of lanthanide containing borates LnM(BO{sub 3}){sub 2} (Ln=Y, Ho–Lu; M=Sc, Cr)

The synthesis, crystal structures and magnetic properties of LnM(BO{sub 3}){sub 2} (Ln=Y, Ho–Lu; M=Sc, Cr) were investigated. The LnCr(BO{sub 3}){sub 2} compounds crystallize in the dolomite-type structure with space group R3{sup ¯}, in which the Ln and Cr ions occupy two octahedral sites. From the result of structural analysis, it was found that there is an anti-site disorder between these two sites and its chemical formula is more exactly Ln{sub 1−r}Cr{sub r}[Cr{sub 1−r}Ln{sub r}](BO{sub 3}){sub 2}. On the other hand, the LnSc(BO{sub 3}){sub 2} adopt the calcite-type structure with space group R3{sup ¯}c. The Ln and Sc ions randomly occupy an octahedral site and the chemical formula is represented as (Ln{sub 0.5}Sc{sub 0.5})BO{sub 3}. From the magnetic susceptibility and specific heat measurements, we found that all the LnCr(BO{sub 3}){sub 2} show an antiferromagnetic transition at 6.1–8.1 K. This transition is mainly due to the ordering of Cr{sup 3+} magnetic moments. Among the compounds with magnetic Ln{sup 3+} ions, only YbCr(BO{sub 3}){sub 2} shows an antiferromagnetic ordering of Ln{sup 3+} ion at 2.1 K. - Graphical abstract: The lanthanide containing borates LnM(BO{sub 3}){sub 2} (Ln=Y, Ho–Lu; M=Sc, Cr) have the dolomite-type (Ln=Cr) and calcite-type (Ln=Sc) structures. Both structures are similar tomore » each other except for the difference in the partially or fully disordered arrangements of octahedral sites. At low temperatures, the LnCr(BO{sub 3}){sub 2} compounds show an antiferromagnetic transition due to a long-range ordering of Cr{sup 3+} moments. Among them only YbCr(BO{sub 3}){sub 2} shows an antiferromagnetic ordering of Ln{sup 3+} ion at 2.1 K. Display Omitted - Highlights: • Lanthanide containing borates LnM(BO{sub 3}){sub 2} (Ln=Y, Ho–Lu; M=Sc, Cr) have been synthesized. • LnCr(BO{sub 3}){sub 2} has the dolomite-type structure with an anti-site disorder between Ln and Cr sites. • LnSc(BO{sub 3}){sub 2} has the calcite-type structure in which the Ln and Cr randomly occupy the same site. • LnCr(BO{sub 3}){sub 2} shows an antiferromagnetic transition at 6.1–8.1 K due to the long-range magnetic ordering of Cr{sup 3+} moments. • Only YbCr(BO{sub 3}){sub 2} shows the two-step antiferromagnetic ordering: Cr{sup 3+} (6.1 K) and Yb{sup 3+} (2.1 K)« less
Authors:
; ;
Publication Date:
OSTI Identifier:
22274118
Resource Type:
Journal Article
Resource Relation:
Journal Name: Journal of Solid State Chemistry; Journal Volume: 206; Other Information: Copyright (c) 2013 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
37 INORGANIC, ORGANIC, PHYSICAL AND ANALYTICAL CHEMISTRY; ANTIFERROMAGNETISM; BORATES; CALCITE; CHROMIUM IONS; CRYSTAL STRUCTURE; DOLOMITE; MAGNETIC MOMENTS; MAGNETIC SUSCEPTIBILITY; MAGNETIZATION; RARE EARTHS; SCANDIUM IONS; SPACE GROUPS; SPECIFIC HEAT; SYNTHESIS; YTTERBIUM IONS