Title: The crystal structure and magnetic properties of Ba{sub 2−x}Sr{sub x}Co{sub 2}Fe{sub 12}O{sub 22}

We have synthesized the Ba{sub 2−x}Sr{sub x}Co{sub 2}Fe{sub 12}O{sub 22} samples (x = 0.1, 0.2, 0.3, 0.4, 0.5) by the solid-state reaction method and investigated their crystalline and magnetic properties by X-ray diffractometer (XRD), Mössbauer spectrometer, vibrating sample magnetometer, and network analyzer. XRD patterns show that all samples are rhombohedral with space group R-3m. The lattice constants a{sub 0} and c{sub 0} decrease with Sr substitution due to smaller ion radius of Sr{sup 2+} (1.27 Å) than that of Ba{sup 2+} (1.43 Å). The Mössbauer spectroscopy measurements show that the relative area ratios of Fe ion were maintained constant regardless of the Sr concentration. However, average magnetic hyperfine field slightly increased with the Sr concentration. This observation agrees with the fact that the saturation magnetization (M{sub s}) linearly increases due to the increasing super-exchange interaction, originated from the difference in the ionic radius between Ba{sup 2+} and Sr{sup 2+}. To investigate its properties at high frequency range, all samples were sintered at 1100 °C, and complex permeability and permittivity were measured by network analyzer between 100 MHz and 4 GHz. For x below 0.3, the initial permeability at 100 MHz increases, at higher values of x, its value decreases. Our study shows that magnetic properties of Sr{sup 2+}more » substitution for Ba{sup 2+} in Y-type hexaferrite as well as low magnetic loss less than 0.1 in 1 GHz band, indicating the potential application of Ba{sub 2−x}Sr{sub x}Co{sub 2}Fe{sub 12}O{sub 22} samples for RF and antenna devices in ultra high frequency band.« less
Authors:
; ;  [1]
  1. Department of Physics, Kookmin University, Seoul 136-702 (Korea, Republic of)
Publication Date:
OSTI Identifier:
22273770
Resource Type:
Journal Article
Resource Relation:
Journal Name: Journal of Applied Physics; Journal Volume: 115; Journal Issue: 17; Conference: 55. annual conference on magnetism and magnetic materials, Atlanta, GA (United States), 14-18 Nov 2010; Other Information: (c) 2014 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND SUPERFLUIDITY; ABSORPTION SPECTROSCOPY; BARIUM COMPOUNDS; BARIUM IONS; COBALT COMPOUNDS; CONCENTRATION RATIO; EXCHANGE INTERACTIONS; FERRITES; IRON IONS; LATTICE PARAMETERS; MAGNETIC PROPERTIES; MAGNETIZATION; MOESSBAUER EFFECT; PERMITTIVITY; STRONTIUM COMPOUNDS; STRONTIUM IONS; TRIGONAL LATTICES; VIBRATING SAMPLE MAGNETOMETERS; X-RAY DIFFRACTION