Optical absorption and fluorescence properties of Er{sup 3+}/Yb{sup 3+} codoped lead bismuth alumina borate glasses
Lead bismuth alumina borate glasses codoped with Er{sup 3+}/Yb{sup 3+} were prepared by melt quenching technique. Optical absorption, FTIR and photoluminescence spectra of these glasses have been studied. Judd-Ofelt theory has been applied to to the f ↔ f transitions for evaluating Ω{sub 2}, Ω{sub 4} and Ω{sub 6} parameters. Radiative properties like branching ratio β{sub r} and the radiative life time τ{sub R} have been determined on the basis of Judd-Ofelt theory. Upconversion emissions have been observed under 980nm laser excitation at room temperature. Green and red up-conversion emissions are centered at 530, 550 and 656 nm corresponding to {sup 2}H{sub 11/2}→{sup 4}I{sub 15/2}, {sup 4}S{sub 3/2}→{sup 4}I{sub 15/2} and {sup 4}F{sub 9/2}→{sup 4}I{sub 15/2} transitions of Er{sup 3+} respectively. The results obtained are discussed quantitatively based on the energy transfer between Yb{sup 3+} and Er{sup 3+}.
- OSTI ID:
- 22271038
- Journal Information:
- AIP Conference Proceedings, Vol. 1591, Issue 1; Conference: 58. DAE solid state physics symposium 2013, Patiala, Punjab (India), 17-21 Dec 2013; Other Information: (c) 2014 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Optical properties and energy transfer processes of Ho{sup 3+}/Er{sup 3+}- codoped fluorotellurite glass under 1550 nm excitation for 2.0 μm applications
Frequency upconversion properties of Er{sup 3+}/Yb{sup 3+}-codoped lead-germanium-bismuth oxide glasses
Related Subjects
SUPERCONDUCTIVITY AND SUPERFLUIDITY
ABSORPTION SPECTRA
ALUMINIUM OXIDES
BISMUTH COMPOUNDS
BORATES
BRANCHING RATIO
EMISSION SPECTRA
ENERGY TRANSFER
ERBIUM IONS
EXCITATION
FLUORESCENCE
FOURIER TRANSFORMATION
GLASS
INFRARED SPECTRA
LEAD COMPOUNDS
PHOTOLUMINESCENCE
QUENCHING
TEMPERATURE RANGE 0273-0400 K
YTTERBIUM IONS