Title: Influence of electron beam irradiation on mechanical and thermal properties of polypropylene/polyamide blend

The effects of electron beam irradiation on the mechanical and thermal properties of polypropylene (PP) and polyamide6 (PA6) blends-with talc 20 wt% as filler, SEBS-g-MAH as compatibilizer, and triallyl isocyanurate as crosslinking agent-were investigated. Although the tensile and flexural moduli and strengths of the PP/PA6 blends with talc, SEBS-g-MAH, and TAIC could be increased by the application of electron beam irradiation, the impact strength was decreased. Ddifferential scanning calorimetryer measurements showed that the melting temperatures of all PP/PA6 blends were decreased with increases in the electron beam irradiationdose. From dynamic mechanical analyzer results, a storage modulus curve in the plateau region was observed only in the PP/PA6 blends with talc, SEBS-g-MAH, and TAIC; the storage modulus increased with increasing electron beam irradiation dose, indicating that the three-dimensional network developed gradually in the more amorphous PA6. As a result, the most significant improvement observed in heat distortion tests under high load (1.8 MPa) occurred at 200 kGy.
Authors:
 [1] ;  [2]
  1. Hitachi Chemical Co., Ltd., 1150 Goshomiya, Chikusei, Ibaraki 308-8524, Japan and Department of Materials Science, School of Engineering, The University of Shiga Prefecture, 2500 Hassaka-cho, Hikone, 522-8533, Shiga (Japan)
  2. Department of Materials Science, School of Engineering, The University of Shiga Prefecture, 2500 Hassaka-cho, Hikone, 522-8533, Shiga (Japan)
Publication Date:
OSTI Identifier:
22270993
Resource Type:
Journal Article
Resource Relation:
Journal Name: AIP Conference Proceedings; Journal Volume: 1593; Journal Issue: 1; Conference: PPS-29: 29. international conference of the Polymer Processing Society, Nuremberg (Germany), 15-19 Jul 2013; Other Information: (c) 2014 American Institute of Physics; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
36 MATERIALS SCIENCE; 75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND SUPERFLUIDITY; AMORPHOUS STATE; CALORIMETRY; CROSS-LINKING; DIFFERENTIAL THERMAL ANALYSIS; ELECTRON BEAMS; FILLERS; IMPACT STRENGTH; IRRADIATION; MELTING POINTS; POLYAMIDES; POLYPROPYLENE; RADIATION DOSES; RADIATION EFFECTS; TALC