Title: Evaluation of the effect of organic pro-degradant concentration in polypropylene exposed to the natural ageing

The production and consumption of plastics in the last decade has recorded a remarkable increase in the scientific and industrial interest in environmentally degradable polymer (EDPs). Polymers wastes are deposited improperly, such as dumps, landfills, rivers and seas, causing a serious problem by the accumulation in the environment. The abiotic processes, like the photodegradation, are the most efficient occurring in the open environmental, where the polymers undergo degradation from the action of sunlight that result from direct exposure to solar radiation, however depend of the type of chemical ageing, which is the principal component of climatic ageing. The subject of this work is to study the influence of concentration of organic pro-degradant (1, 2 and 3 % w/w) in the polypropylene (PP) exposed in natural ageing. PP samples with and without the additive were processed in plates square form, obtained by thermal compression molding (TCM) using a press at 200°C under 2 tons for 5 min, and then were exposed at natural ageing during 120 days. The presence of organic additive influenced on PP degradability, this fact was assessed by changes in the thermal and morphology properties of the samples after 120 days of natural ageing. Scanning Electronic Microscopy (SEM)more » results of the morphological surface of the modified PP samples showed greater degradation photochemical oxidative when compared to neat PP, due to increase of rugosity and formation of microvoids. PP samples with different pro-degradant concentration under natural ageing presented a degree of crystallinity, obtained by Differential Scanning Calorimeter (DSC) increases in comparing the neat PP.« less
Authors:
; ; ; ;  [1]
  1. Engineering School/Laboratory of Polymeric Materials, Federal University of Rio Grande do Sul, Porto Alegre (Brazil)
Publication Date:
OSTI Identifier:
22270977
Resource Type:
Journal Article
Resource Relation:
Journal Name: AIP Conference Proceedings; Journal Volume: 1593; Journal Issue: 1; Conference: PPS-29: 29. international conference of the Polymer Processing Society, Nuremberg (Germany), 15-19 Jul 2013; Other Information: (c) 2014 American Institute of Physics; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
36 MATERIALS SCIENCE; ADDITIVES; AGING; CALORIMETRY; COMPARATIVE EVALUATIONS; COMPRESSION; CONCENTRATION RATIO; DIFFERENTIAL THERMAL ANALYSIS; MOLDING; MORPHOLOGY; OXIDATION; PLASTICS; POLYPROPYLENE; SCANNING ELECTRON MICROSCOPY; SOLAR RADIATION; SURFACES