Relaxation behavior of oxygen deficient strontium manganite
Conduction behavior of nanocrystalline oxygen deficient ceramic-SrMnO{sub 3–δ}(δ∼0.14) has been studied. The structural analysis of nano-SrMnO{sub 2.86} follows hexagonal unit cell structure with P6{sub 3}/mmc (194) space group belonging to 6/mmm point group with 4H – layered type hexagonal-cubic layers. The system have lattice parameters; a = 5.437(92) Å, c = 9.072(92) Å, c/a∼1.66 (85) with α =90° γ= 120° and cell volume, V= 232.35(18). The relaxation times estimated from complex impedance and modulus relaxation spectrum, show the thermally activated system with corresponding activation energies as 0.66 eV and 0.51 eV The stretching factor ‘β’ from the scaled modulus spectrum shows the poly-dispersive non-Debye nature of the system. The hopping number ‘n’ shows the influence of ionic charge carriers which controls the conduction mechanism of nano-SrMnO{sub 2.86}.
- OSTI ID:
- 22269319
- Journal Information:
- AIP Conference Proceedings, Vol. 1591, Issue 1; Conference: 58. DAE solid state physics symposium 2013, Patiala, Punjab (India), 17-21 Dec 2013; Other Information: (c) 2014 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
The Zintl phases AIn2As2 (A = Ca, Sr, Ba): new topological insulators and thermoelectric material candidates
Nanostructural and electronic properties of polytypes in InN nanocolumns