Title: Synthesis of silver nanoparticles by chemical reduction at various fraction of MSA and their structure characterization

Nanosilver is currently one of the most common engineered nanomaterials and is used in many applications that lead to the release of silver nanoparticles and silver ions into aqueous systems. Nanosilver also possesses enhanced antimicrobial activity and bioavailability that may less environmental risk compared with other manufactured nanomaterials. Described in this research are the synthesis of silver nanoparticle produced by chemical reduction from silver nitrate (AgNO{sub 3}) solution. As a reducing agent, Sodium Borohydride (NaBH{sub 4}) was used and mercaptosuccinic Acid (MSA) as stabilizer to prevent the nanoparticle from aglomerating. It was also used two kinds of solvent, they are water and methanol. In typical experiment MSA was dissolve in methanol with a number of variation of molarity i.e. 0,03 M, 0,06 M, 0,12 M, 0,15 M, and the mixture was kept under vigorous stirring in an ice bath. A solution of silver nitrate of 340 mg in 6,792 ml water was added. A freshly prepared aqueous solution of sodium borohydride (756,6 mL in 100 mL of water) was added drop wisely. The solution was kept for half an hour for stirring and were allowed to settle down in methanol. The obtained samples then characterized by means of x-ray diffractometer,more » and scanning electron microscopy, as well as transmission electron microscopy to obtain their structures of silver nanoparticles, morphology, and sizes. It is shown that diameter of silver nanoparticle sized about 24.3 nm (Ag@MSA 0.03 M), 20.4 nm (Ag@MSA 0.06 M), 16.8 nm (Ag@MSA 0.12 M), 16.9 nm (Ag@MSA 0.15 M) which was calculated by Scherrer formula by taking the FWHM from fitting to Gaussian. The phases and lattice parameter showed that there is no significant change in its volume by increasing molarity of stabilizer. In contrast, the size of particles is decreasing.« less
Authors:
; ; ;  [1]
  1. Department of Physics, Faculty of Mathematics and Natural Sciences, Universitas Negeri Malang (UM), Jl. Semarang No. 5 Malang 65145 (Indonesia)
Publication Date:
OSTI Identifier:
22265972
Resource Type:
Journal Article
Resource Relation:
Journal Name: AIP Conference Proceedings; Journal Volume: 1589; Journal Issue: 1; Conference: ICMNS 2012: 4. international conference on mathematics and natural sciences: Science for health, food and sustainable energy, Bandung (Indonesia), 8-9 Nov 2012; Other Information: (c) 2014 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
37 INORGANIC, ORGANIC, PHYSICAL AND ANALYTICAL CHEMISTRY; 77 NANOSCIENCE AND NANOTECHNOLOGY; AQUEOUS SOLUTIONS; LATTICE PARAMETERS; METHANOL; NANOSTRUCTURES; PARTICLES; REDUCING AGENTS; SCANNING ELECTRON MICROSCOPY; SILVER; SILVER IONS; SILVER NITRATES; SODIUM; SOLVENTS; SYNTHESIS; TRANSMISSION ELECTRON MICROSCOPY; WATER; X-RAY DIFFRACTOMETERS