Title: Annealing effects on structural, electrical and optical properties of antimony-tinoxide thin films deposited by sol gel dip coating technique

Antimony-doped tin dioxide possess interesting physical and chemical properties. These properties have a wide range of applications such as catalysis and optoelectronic devices. In the present study, antimony-doped tin oxide (SnO2:Sb) thin films were deposited on the quartz substrates by sol-gel dip coating technique. The films were annealed at temperatures 350°C, 550°C and 850°C in air for 2 hours. The structure and surface morphologies were observed by X-ray diffraction (XRD) and Scanning electron microscopy (SEM). XRD patterns shows tetragonal structure for the SnO2:Sb films annealed at different temperatures. Crystallite size increased from 6 to 14 nm as annealing temperature increased from 350°C to 850°C. SEM studies reveals crack free and smooth surface for all the films. The grains are found to be homogenously distributed for films annealed at higher temperature. The electrical conductivity of the films annealed at 350°C and 550°C decreased and increased for the films annealed at 850°C. The optical properties of the films were investigated in the UV-visible-NIR region (200-900 nm) using UV spectra. The transmittance of the films decreased for films annealed at higher temperature. The optical energy band gap values (4.13 eV-4.83 eV) increased with the increase in annealing temperature.
Authors:
; ; ;  [1]
  1. Thin film Laboratory, Post Graduate and Research Department of Physics, Mar Ivanios College, Thiruvananthapuram 695 015 (India)
Publication Date:
OSTI Identifier:
22264025
Resource Type:
Journal Article
Resource Relation:
Journal Name: AIP Conference Proceedings; Journal Volume: 1576; Journal Issue: 1; Conference: OMTAT 2013: 2. international conference on optoelectronic materials and thin films for advanced technology, Kochi, Kerala (India), 3-5 Jan 2013; Other Information: (c) 2014 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND SUPERFLUIDITY; 36 MATERIALS SCIENCE; ANNEALING; ANTIMONY; CHEMICAL PROPERTIES; DEPOSITS; DIP COATING; DOPED MATERIALS; ELECTRIC CONDUCTIVITY; OPTICAL PROPERTIES; SCANNING ELECTRON MICROSCOPY; SOL-GEL PROCESS; SUBSTRATES; THIN FILMS; TIN OXIDES; X-RAY DIFFRACTION