Title: Analysis of surface integrity of grinded gears using Barkhausen noise analysis and x-ray diffraction

The contribution is focused to present results of study grinded gears made of 18CrNiMo7-6 steel used in the wind power plant for support (service) purposes. These gears were case-hardened due to standard hard case and soft core formation. This heat treatment increases wear resistance and fatigue strength of machine parts. During serial production some troubles with surface integrity have occurred. When solving complex problems lots of samples were prepared. For grinding of gears were used different parameters of cutting speed, number of material removal and lots from different subsuppliers. Material characterization was carried out using Barkhausen noise analysis (BNA) device; X-ray diffraction (XRD) measurement of surface residual stresses was done as well. Depth profile of measured characteristics, e.g. magnetoelastic parameter and residual stress was obtained by step by step layers' removing using electrolytic etching. BNA software Viewscan was used to measure magnetizing frequency sweep (MFS) and magnetizing voltage sweep (MVS). Scanning of Magnetoelastic parameter (MP) endwise individual teeth were also carried out with Viewscan. These measurements were done to find problematic surface areas after grinding such as thermal damaged locations. Plots of the hardness and thickness of case-hardened layer on cross sections were measurered as well. Evaluation of structure ofmore » subsurface case-hardened layer and core was made on etched metallographic patterns. The aim of performed measurements was to find correlation between conditions of grinding, residual stresses and structural and magnetoelastic parameters. Based on correlation of measured values and technological parameters optimizing the production of gears will be done.« less
Authors:
;  [1] ;  [2]
  1. Institute for Nanomaterials, Advanced Technologies and Innovation, Technical University of Liberec (Czech Republic)
  2. Department of Analytic Services, PCS s.r.o. (Czech Republic)
Publication Date:
OSTI Identifier:
22263743
Resource Type:
Journal Article
Resource Relation:
Journal Name: AIP Conference Proceedings; Journal Volume: 1581; Journal Issue: 1; Conference: 40. annual review of progress in quantitative nondestructive evaluation, Baltimore, MD (United States), 21-26 Jul 2013, 10. international conference on Barkhausen noise and micromagnetic testing, Baltimore, MD (United States), 21-26 Jul 2013; Other Information: (c) 2014 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
71 CLASSICAL AND QUANTUM MECHANICS, GENERAL PHYSICS; CROSS SECTIONS; ELECTRIC POTENTIAL; GRINDING; HEAT TREATMENTS; LAYERS; RESIDUAL STRESSES; SURFACE AREA; SURFACES; WEAR RESISTANCE; WIND POWER PLANTS; X-RAY DIFFRACTION