Title: A comparative wear study on Al-Li and Al-Li/SiC composite

Aluminum-lithium based unreinforced (Al-8090) alloy and Al-8090/SiCp/17 vol.% metal matrix composite produced by extrusion after spray co-deposition. A dry ball-on disk wear test was carried out for both alloy and composite. The tests were performed against an Al{sub 2}O{sub 3} ball, 10 mm in diameter, at room temperature and in laboratory air conditions with a relative humidity of 40-60%. Sliding speed was chosen as 1.0 ms{sup −1} and normal loads of 1.0, 3.0 and 5.0 N were employed at a constant sliding distance of 1000 m. The wear damage on the specimens was evaluated via measurement of wear depth and diameter. Microstructural and wear characterization was carried out via scanning electron microscopy (SEM). The results showed that wear loss of the Al-8090/SiC composite was less than that of the Al-8090 matrix alloy. Plastic deformation observed on the wear surface of the composite and the matrix alloy, and the higher the applied load the greater the plastic deformation. Scanning electron microscopy examinations of wear tracks also reveal that delamination fracture was the dominant wear mechanism during the wear progression. Friction coefficient was maximum at the low applied load in the case of the Al-8090/SiC composite while a gradual increase was observedmore » with applied load for the matrix alloy.« less
Authors:
; ;  [1]
  1. Sakarya University Engineering Faculty, Department of Metallurgical and Materials Engineering, Esentepe Campus, 54187, Sakarya (Turkey)
Publication Date:
OSTI Identifier:
22261715
Resource Type:
Journal Article
Resource Relation:
Journal Name: AIP Conference Proceedings; Journal Volume: 1569; Journal Issue: 1; Conference: 3. international advances in applied physics and materials science congress, Antalya (Turkey), 24-28 Apr 2013; Other Information: (c) 2013 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
36 MATERIALS SCIENCE; ALLOYS; ALUMINIUM; HUMIDITY; LITHIUM; MICROSTRUCTURE; PLASTICITY; SCANNING ELECTRON MICROSCOPY; SILICON CARBIDES