Title: Influence of core size on the upconversion luminescence properties of spherical Gd{sub 2}O{sub 3}:Yb{sup 3+}/Er{sup 3+}@SiO{sub 2} particles with core-shell structures

Spherical SiO{sub 2} particles with different sizes (30, 80, 120, and 180 nm) have been coated with Gd{sub 2}O{sub 3}:Yb{sup 3+}/Er{sup 3+} layers by a heterogeneous precipitation method, leading to the formation of core-shell structural Gd{sub 2}O{sub 3}:Yb{sup 3+}/Er{sup 3+}@SiO{sub 2} particles. The samples were characterized by using X-ray diffraction, field emission scanning electron microscopy, transmission electron microscopy, upconversion (UC) emission spectra, and fluorescent dynamical analysis. The obtained core-shell particles have perfect spherical shape with narrow size distribution. Under the excitation of 980 nm diode laser, the core-shell samples showed size-dependent upconversion luminescence (UCL) properties. The inner SiO{sub 2} cores in core-shell samples were proved to have limited effect on the total UCL intensities of Er{sup 3+} ions. The UCL intensities of core-shell particles were demonstrated much higher than the values obtained in pure Gd{sub 2}O{sub 3}:Yb{sup 3+}/Er{sup 3+} with the same phosphor volume. The dependence of the specific area of a UCL shell on the size of its inner SiO{sub 2} particle was calculated and analyzed for the first time. It was confirmed that the surface effect came from the outer surfaces of emitting shells is dominant in influencing the UCL property in the core-shell samples. Three-photon UC processes for themore » green emissions were observed in the samples with small sizes of SiO{sub 2} cores. The results of dynamical analysis illustrated that more nonradiative relaxation occurred in the core-shell samples with smaller SiO{sub 2} core sizes.« less
Authors:
; ; ; ;  [1]
  1. State Key Laboratory on Integrated Optoelectronics, College of Electronic Science and Engineering, Jilin University, Changchun 130012 (China)
Publication Date:
OSTI Identifier:
22259289
Resource Type:
Journal Article
Resource Relation:
Journal Name: Journal of Applied Physics; Journal Volume: 114; Journal Issue: 18; Other Information: (c) 2013 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
36 MATERIALS SCIENCE; 71 CLASSICAL AND QUANTUM MECHANICS, GENERAL PHYSICS; EMISSION SPECTRA; ERBIUM IONS; FIELD EMISSION; FLUORESCENCE; GADOLINIUM OXIDES; PARTICLES; SCANNING ELECTRON MICROSCOPY; SILICA; SILICON OXIDES; TRANSMISSION ELECTRON MICROSCOPY; X-RAY DIFFRACTION; YTTERBIUM IONS