Title: Time-resolved measurement of photon emission during fast crack propagation in three-point bending fracture of silica glass and soda lime glass

Simultaneous time-resolved measurements of photon emission (PE) and fast crack propagation upon bending fracture were conducted in silica glass and soda lime glass. Observation of fracture surfaces revealed that macroscopic crack propagation behavior was similar between the silica glass and soda lime glass when fracture loads for these specimens were comparable and cracks propagated without branching. However, a large difference in the PE characteristics was found between the two glasses. In silica glass, PE (645–655 nm) was observed during the entire crack propagation process, whereas intense PE (430–490 nm and 500–600 nm) was observed during the initial stages of propagation. In contrast, only weak PE was detected in soda lime glass. These results show that there is a large difference in the atomic processes involved in fast crack propagation between these glasses, and that PE can be used to study brittle fracture on the atomic scale.
Authors:
; ;  [1]
  1. Department of Metallurgy and Ceramics Science, Tokyo Institute of Technology, 2-12-1-S7-13 Ookayama, Meguro-ku, Tokyo 152-8550 (Japan)
Publication Date:
OSTI Identifier:
22257036
Resource Type:
Journal Article
Resource Relation:
Journal Name: Applied Physics Letters; Journal Volume: 104; Journal Issue: 10; Other Information: (c) 2014 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
36 MATERIALS SCIENCE; CRACK PROPAGATION; CRACKS; FRACTURES; GLASS; PHOTON EMISSION; SILICA; SODIUM CARBONATES; TIME RESOLUTION