Title: Investigation of a pulsed current annealing method in reusing MOSFET dosimeters for in vivo IMRT dosimetry

Purpose: To explore the feasibility of pulsed current annealing in reusing metal oxide semiconductor field-effect transistor (MOSFET) dosimeters forin vivo intensity modulated radiation therapy (IMRT) dosimetry. Methods: Several MOSFETs were irradiated atd{sub max} using a 6 MV x-ray beam with 5 V on the gate and annealed with zero bias at room temperature. The percentage recovery of threshold voltage shift during multiple irradiation-annealing cycles was evaluated. Key dosimetry characteristics of the annealed MOSFET such as the dosimeter's sensitivity, reproducibility, dose linearity, and linearity of response within the dynamic range were investigated. The initial results of using the annealed MOSFETs for IMRT dosimetry practice were also presented. Results: More than 95% of threshold voltage shift can be recovered after 24-pulse current continuous annealing in 16 min. The mean sensitivity degradation was found to be 1.28%, ranging from 1.17% to 1.52%, during multiple annealing procedures. Other important characteristics of the annealed MOSFET remained nearly consistent before and after annealing. Our results showed there was no statistically significant difference between the annealed MOSFETs and their control samples in absolute dose measurements for IMRT QA (p = 0.99). The MOSFET measurements agreed with the ion chamber results on an average of 0.16% ± 0.64%.more » Conclusions: Pulsed current annealing provides a practical option for reusing MOSFETs to extend their operational lifetime. The current annealing circuit can be integrated into the reader, making the annealing procedure fully automatic.« less
Authors:
; ;  [1] ;  [2]
  1. Department of Radiation Oncology, Sun Yat-Sen University Cancer Center and State Key Laboratory of Oncology in Southern China, Collaborative Innovation Center of Cancer Medicine, Guangzhou 510060 (China)
  2. Centre for Medical Radiation Physics, University of Wollongong, Wollongong, NSW 2522 (Australia)
Publication Date:
OSTI Identifier:
22250676
Resource Type:
Journal Article
Resource Relation:
Journal Name: Medical Physics; Journal Volume: 41; Journal Issue: 5; Other Information: (c) 2014 American Association of Physicists in Medicine; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
62 RADIOLOGY AND NUCLEAR MEDICINE; ANNEALING; DOSEMETERS; DOSIMETRY; ELECTRIC POTENTIAL; IN VIVO; IRRADIATION; MOSFET; OXIDES; RADIATION DOSES; RADIOTHERAPY; SEMICONDUCTOR MATERIALS