A simple method for the measurement of reflective foil emissivity
Reflective metal foil is widely used to reduce radiative heat transfer within the roof space of buildings. Such foils are typically mass-produced by vapor-deposition of a thin metallic coating onto a variety of substrates, ranging from plastic-coated reinforced paper to 'bubble-wrap'. Although the emissivity of such surfaces is almost negligible in the thermal infrared, typically less than 0.03, an insufficiently thick metal coating, or organic contamination of the surface, can significantly increase this value. To ensure that the quality of the installed insulation is satisfactory, Australian building code AS/NZS 4201.5:1994 requires a practical agreed method for measurement of the emissivity, and the standard ASTM-E408 is implied. Unfortunately this standard is not a 'primary method' and requires the use of specified expensive apparatus and calibrated reference materials. At NMIA we have developed a simple primary technique, based on an apparatus to thermally modulate the sample and record the apparent modulation in infra-red radiance with commercially available radiation thermometers. The method achieves an absolute accuracy in the emissivity of approximately 0.004 (k=2). This paper theoretically analyses the equivalence between the thermal emissivity measured in this manner, the effective thermal emissivity in application, and the apparent emissivity measured in accordance with ASTM-E408.
- OSTI ID:
- 22218044
- Journal Information:
- AIP Conference Proceedings, Vol. 1552, Issue 1; Conference: 9. international temperature symposium, Los Angeles, CA (United States), 19-23 Mar 2012; Other Information: (c) 2013 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
PERFORMANCE EVALUATION OF A SUSTAINABLE AND ENERGY EFFICIENT RE-ROOFING TECHNOLOGY USING FIELD-TEST DATA
DESIGN AND OPERATION OF 1800 F PUMPED BOILING RUBIDIUM LOOP SYSTEM AND DETERMINATION OF DENSITY AND VAPOR PRESSURE RUBIDIUM BETWEEN 174 AND 1800 F. Space Power Systems Technology Studies: Rubidium, Corrosion and Physical Properties Evaluation Program. Final Report (Report No. 16), February 1, 1960 through May 31, 1961