Simple solvothermal synthesis of hydrophobic magnetic monodispersed Fe{sub 3}O{sub 4} nanoparticles

Journal Article · Fri Feb 15 00:00:00 EST 2013 · Materials Research Bulletin

DOI:https://doi.org/10.1016/J.MATERRESBULL.2012.10.060· OSTI ID:22215812

Liu, Jing; Wang, Lu ^[1]; Wang, Jing ^[1]; Zhang, Lantong ^[1]

---

1. School of Pharmaceutical Sciences, Hebei Medical University, Shijiazhuang 050017 (China)

Graphical abstract: A facile method to produce monodispersed magnetite nanoparticles is based on the solvothermal reaction of iron acetylacetonate (Fe(acac)3) decomposition. The sizes ranged from 7 to 12 nm, which could be controlled by adjusting the volume ratio of oleylamine to n-hexane. Display Omitted Highlights: ► The solvethermal reaction of Fe(acac){sub 3} decomposition was carried out at mild temperature in the presence of oleylamine and n-hexane. ► The size of nanocrystals is controlled by adjusting the volume ratio of oleylamine to n-hexane. ► The low-boiling-point solvent n-hexane offered autogenous pressure parameter after gasified in the reaction temperature. ► The as prepared hydrophobic monodisperse Fe{sub 3}O{sub 4} NPs can be used to prepare the magnetic micelles for future biomedical applications. -- Abstract: A new solvothermal method is proposed for the preparation of Fe{sub 3}O{sub 4} nanoparticles (NPs) from iron acetylacetonate in the presence of oleylamine and n-hexane. The products are characterized by X-ray powder diffraction, infrared (IR) spectroscopy, transmission electron microscopy, thermogravimetry/differential thermogravimetry (TG/DTG) analysis, and vibrating sample magnetometery. The new procedure yields superparamagnetic monodispersed Fe{sub 3}O{sub 4} particles with sizes ranging from 7 nm to 12 nm. The nanocrystal sizes are controlled by adjusting the volume ratio of oleylamine to n-hexane. IR and TG/DTG analyses indicate that the oleylamine molecules, as stabilizers, are adsorbed on the surface of Fe{sub 3}O{sub 4} NPs as bilayer adsorption models. The surface adsorption quantities of oleylamine on 7.5 and 10.4 nm-diameter Fe{sub 3}O{sub 4} NPs are 18% and 11%, respectively. The hydrophobic surface of the obtained nanocrystals is passivated by adsorbed organic solvent molecules. These molecules provide stability against agglomeration, enable solubility in nonpolar solvents, and allow the formation of magnetic polymer micelles.

• OSTI ID: 22215812
• Journal Information: Materials Research Bulletin, Vol. 48, Issue 2; Other Information: Copyright (c) 2012 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0025-5408
• Country of Publication: United States
• Language: English

Related Subjects

36 MATERIALS SCIENCE
ADSORPTION
AGGLOMERATION
BOILING POINTS
DECOMPOSITION
FERRITES
HEXANE
INFRARED SPECTRA
IRON OXIDES
LAYERS
MAGNETIC PROPERTIES
MAGNETITE
NANOSTRUCTURES
ORGANIC SOLVENTS
POLYMERS
SUPERPARAMAGNETISM
SURFACES
SYNTHESIS
THERMAL GRAVIMETRIC ANALYSIS
TRANSMISSION ELECTRON MICROSCOPY
X-RAY DIFFRACTION