Influence of Ni-Cr substitution on the magnetic and electric properties of magnesium ferrite nanomaterials
- Surface and Solid State Chemistry Laboratory, Department of Chemistry, Quaid-i-Azam University, Islamabad 45320 (Pakistan)
- Wolfson Centre for Magnetics, School of Engineering, Cardiff University, Cardiff CF24 3AA (United Kingdom)
- Ames Laboratory of US Department of Energy, Ames, IA 50011 (United States)
Graphical abstract: Variation of saturation magnetization (M{sub S}) and magnetocrystalline anisotropy coefficient (K{sub 1}) with Ni-Cr content for Mg{sub 1-x}Ni{sub x}Cr{sub x}Fe{sub 2-x}O{sub 4} (x = 0.0-0.5). Highlights: Black-Right-Pointing-Pointer Mg{sub 1-x}Ni{sub x}Cr{sub x}Fe{sub 2-x}O{sub 4} are synthesized by novel PEG assisted microemulsion method. Black-Right-Pointing-Pointer High field regime of M-H loops are modeled using Law of Approach to saturation. Black-Right-Pointing-Pointer A considerable increase in the value of M{sub S} from 148 kA/m to 206 kA/m is achieved Black-Right-Pointing-Pointer {rho}{sup RT} enhanced to the order of 10{sup 9} {Omega}cm at potential operational range around 300 K. -- Abstract: The effect of variation of composition on the structural, morphological, magnetic and electric properties of Mg{sub 1-x}Ni{sub x}Cr{sub x}Fe{sub 2-x}O{sub 4} (x = 0.0-0.5) nanocrystallites is presented. The samples were prepared by novel polyethylene glycol (PEG) assisted microemulsion method with average crystallite size of 15-47 nm. The microstructure, chemical, and phase analyses of the samples were studied by the scanning electron microscopy (SEM), atomic force microscopy (AFM), energy dispersive X-ray fluorescence (ED-XRF), and X-ray diffraction (XRD). Compositional variation greatly affected the magnetic and structural properties. The high-field regimes of the magnetic loops are modelled using the Law of Approach (LOA) to saturation in order to extract information about their anisotropy and the saturation magnetization. Thermal demagnetization measurements are carried out using VSM and significant enhancement of the Curie temperature from 681 K to 832 K has been achieved by substitution of different contents of Ni-Cr. The dc-electrical resistivity ({rho}{sup RT}) at potential operational range around 300 K is increased from 7.5 Multiplication-Sign 10{sup 8} to 4.85 Multiplication-Sign 10{sup 9} {Omega}cm with the increase in Ni-Cr contents. Moreover, the results of the present study provide sufficient evidence to show that the electric and magnetic properties of Mg-ferrite have been improved significantly by substituting low contents of Ni-Cr.
- OSTI ID:
- 22212422
- Journal Information:
- Materials Research Bulletin, Vol. 47, Issue 2; Other Information: Copyright (c) 2011 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0025-5408
- Country of Publication:
- United States
- Language:
- English
Similar Records
High magnetic ordering temperature in the perovskites Sr{sub 4-x}La{sub x}Fe{sub 3}ReO{sub 12} (x=0.0, 1.0, 2.0)
Rare-earth chromium gallides RE{sub 4}CrGa{sub 12} (RE=Tb-Tm)
Related Subjects
77 NANOSCIENCE AND NANOTECHNOLOGY
ATOMIC FORCE MICROSCOPY
ELECTRIC CONDUCTIVITY
FERRITE
FERRITES
FLUORESCENCE
MAGNESIUM
MAGNETIC PROPERTIES
MAGNETIZATION
MICROEMULSIONS
MICROSTRUCTURE
NANOSTRUCTURES
POLYETHYLENE GLYCOLS
SCANNING ELECTRON MICROSCOPY
SPECTROSCOPY
SYNTHESIS
X-RAY DIFFRACTION
X-RAY FLUORESCENCE ANALYSIS