Title: Electron microscopy of GaAs-based structures with InAs and As quantum dots separated by an AlAs barrier

Electron microscopy studies of GaAs-based structures grown by molecular beam epitaxy and containing arrays of semiconductor InAs quantum dots and metal As quantum dots are performed. The array of InAs quantum dots is formed by the Stranski-Krastanov mechanism and consists of vertically coupled pairs of quantum dots separated by a GaAs spacer 10 nm thick. To separate the arrays of semiconductor and metal quantum dots and to prevent diffusion-induced mixing, the array of InAs quantum dots is overgrown with an AlAs barrier layer 5 or 10 nm thick, after which a GaAs layer is grown at a comparatively low temperature (180 Degree-Sign C). The array of As quantum dots is formed in an As-enriched layer of the low-temperature GaAs by means of post-growth annealing at 400-760 Degree-Sign C for 15 min. It is established that the AlAs barrier layer has a surface profile corresponding to that of a subbarrier layer with InAs quantum dots. The presence of such a profile causes the formation of V-shaped structural defects upon subsequent overgrowth with the GaAs layer. Besides, it was obtained that AlAs layer is thinned over the InAs quantum dots tops. It is shown that the AlAs barrier layer in the regionsmore » between the InAs quantum dots effectively prevents the starting diffusion of excess As at annealing temperatures up to 600 Degree-Sign C. However, the concentration of mechanical stresses and the reduced thickness of the AlAs barrier layer near the tops of the InAs quantum dots lead to local barrier breakthroughs and the diffusion of As quantum dots into the region of coupled pairs of InAs quantum dots at higher annealing temperatures.« less
Authors:
; ;  [1] ; ; ;  [2]
  1. Russian Academy of Sciences, Ioffe Physical-Technical Institute (Russian Federation)
  2. Russian Academy of Sciences, Rzhanov Institute of Semiconductor Physics, Siberian Branch (Russian Federation)
Publication Date:
OSTI Identifier:
22210546
Resource Type:
Journal Article
Resource Relation:
Journal Name: Semiconductors; Journal Volume: 47; Journal Issue: 9; Other Information: Copyright (c) 2013 Pleiades Publishing, Ltd.; http://www.springer-ny.com; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
36 MATERIALS SCIENCE; 77 NANOSCIENCE AND NANOTECHNOLOGY; ALUMINIUM ARSENIDES; ELECTRON MICROSCOPY; GALLIUM ARSENIDES; INDIUM ARSENIDES; MOLECULAR BEAM EPITAXY; QUANTUM DOTS; SEMICONDUCTOR MATERIALS; THICKNESS