Title: Ti{sub 5}O{sub 5} superstructures of cubic titanium monoxide

A cubic model is proposed for the Ti{sub 5}O{sub 5} (Ti{sub 5} Black-Small-Square O{sub 5}{open_square} {identical_to} Ti{sub 90} Black-Small-Square {sub 18}O{sub 90}{open_square}{sub 18}) superstructure of nonstoichiometric titanium monoxide Ti{sub x}O{sub z} with double imperfection. The unit cell of the cubic Ti{sub 5}O{sub 5} superstructure has the threefold lattice parameter of the unit cell of the basis disordered B1 structure of Ti{sub x}O{sub z} monoxide and belongs to space group Pm 3-bar m . The channel of the disorder-order transition, i.e., Ti{sub x}O{sub z} (space group Fm 3-bar m)-Ti{sub 5}O{sub 5} (space group Pm 3-bar m), includes 75 superstructure vectors of seven stars (k{sub 10}), (k{sub 7}), (k{sub 6(1)}), (k{sub 6(2)}), (k{sub 4(1)}), (k{sub 4(2)}), and (k{sub 1}). The distribution functions of Ti and O atoms over the sites of the cubic Ti{sub 5}O{sub 5} superstructure are calculated. A comparison of the X-ray and electron diffraction data obtained for ordered TiO{sub 1.087} monoxide with the theoretical simulation results supports the existence of the cubic Ti{sub 5}O{sub 5} superstructure. The cubic (space group Pm 3-bar m) Ti{sub 5}O{sub 5} superstructure is shown to be a high-temperature structure relative to the well-known monoclinic (space group C2/m) superstructure of the same type.
Authors:
 [1]
  1. Russian Academy of Sciences, Institute of Solid-State Chemistry, Ural Branch (Russian Federation)
Publication Date:
OSTI Identifier:
22210511
Resource Type:
Journal Article
Resource Relation:
Journal Name: Journal of Experimental and Theoretical Physics; Journal Volume: 117; Journal Issue: 2; Other Information: Copyright (c) 2013 Pleiades Publishing, Ltd.; http://www.springer-ny.com; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND SUPERFLUIDITY; ATOMS; COMPARATIVE EVALUATIONS; DEFECTS; DISTRIBUTION FUNCTIONS; ELECTRON DIFFRACTION; LATTICE PARAMETERS; MONOCLINIC LATTICES; SIMULATION; SPACE GROUPS; TEMPERATURE RANGE 0400-1000 K; TITANIUM OXIDES; X RADIATION