Preparation and characterization of ZnO-TiO{sub 2} nanocomposite for photocatalytic disinfection of bacteria and detoxification of cyanide under visible light
- Department of Chemistry, Annamalai University, Annamalainagar 608002, Tamilnadu (India)
- Division of Microbiology, Rajah Muthiah Medical College, Annamalai University, Annamalainagar 608002, Tamilnadu (India)
Highlights: {yields} ZnO-TiO{sub 2} nanocomposite, obtained by modified ammonia-evaporation-induced synthetic method, absorbs visible light. {yields} ZnO-TiO{sub 2} nanoparticles catalyze bacteria disinfection and cyanide detoxification under sunlight. {yields} ZnO-TiO{sub 2} nanocomposite is selective in photocatalysis. -- Abstract: ZnO-TiO{sub 2} nanocomposite was prepared by modified ammonia-evaporation-induced synthetic method. It was characterized by powder X-ray diffraction, transmission electron microscopy, selected area electron diffraction, and energy dispersive X-ray, UV-visible diffuse reflectance, photoluminescence and electrochemical impedance spectroscopies. Incorporation of ZnO leads to visible light absorption, larger charge transfer resistance and lower capacitance. The nanocomposite effectively catalyzes the inactivation of E. coli under visible light. Further, the prepared nanocomposite displays selective photocatalysis. While its photocatalytic efficiency to detoxify cyanide with visible light is higher than that of TiO{sub 2} P25, its efficiency to degrade methylene blue, sunset yellow and rhodamine B dyes under UV-A light is less than that of TiO{sub 2} P25.
- OSTI ID:
- 22210084
- Journal Information:
- Materials Research Bulletin, Vol. 46, Issue 10; Other Information: Copyright (c) 2011 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0025-5408
- Country of Publication:
- United States
- Language:
- English
Similar Records
Enhanced photoelectrochemical water splitting from Si quantum dots/TiO{sub 2} nanotube arrays composite electrodes
Bi{sub 2}WO{sub 6} photocatalytic films fabricated by layer-by-layer technique from Bi{sub 2}WO{sub 6} nanoplates and its spectral selectivity