Preparation of cobalt-zinc ferrite (Co{sub 0.8}Zn{sub 0.2}Fe{sub 2}O{sub 4}) nanopowder via combustion method and investigation of its magnetic properties
- Department of Physics, Malek-Ashtar University of Technology, Shahinshahr, 83145-34177 (Iran, Islamic Republic of)
- Department of Physics, Faculty of Science, The University of Isfahan, Esfahan 81746-73441 (Iran, Islamic Republic of)
- Islamic Azad University, Najafabad Branch, Najafabad (Iran, Islamic Republic of)
Research highlights: {yields} Cobalt-zinc ferrite was prepared by combustion method. {yields} Properties of the sample were characterized by several techniques. {yields} Curie temperature was determined to be 350 {sup o}C. -- Abstract: Cobalt-zinc ferrite (Co{sub 0.8}Zn{sub 0.2}Fe{sub 2}O{sub 4}) was prepared by combustion method, using cobalt, zinc and iron nitrates. The crystallinity of the as-burnt powder was developed by annealing at 700 {sup o}C. Crystalline phase was investigated by XRD. Using Williamson-Hall method, the average crystallite sizes for nanoparticles were determined to be about 27 nm before and 37 nm after annealing, and residual stresses for annealed particles were omitted. The morphology of the annealed sample was investigated by TEM and the mean particle size was determined to be about 30 nm. The final stoichiometry of the sample after annealing showed good agreement with the initial stoichiometry using atomic absorption spectrometry. Magnetic properties of the annealed sample such as saturation magnetization, remanence magnetization, and coercivity measured at room temperature were 70 emu/g, 14 emu/g, and 270 Oe, respectively. The Curie temperature of the sample was determined to be 350 {sup o}C using AC-susceptibility technique.
- OSTI ID:
- 22209942
- Journal Information:
- Materials Research Bulletin, Vol. 45, Issue 12; Other Information: Copyright (c) 2010 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0025-5408
- Country of Publication:
- United States
- Language:
- English
Similar Records
Tuning of Magnetic and Optical Properties of Co{sub 0.8}Zn{sub 0.2}Fe{sub 2}O{sub 4} Spinel Ferrite Thin Films Based on Post Annealing Temperature
Structural and Magnetic Studies of Nano-crystalline Ferrites MFe{sub 2}O{sub 4} (M = Zn, Ni, Cu, and Co) Synthesized Via Citrate Gel Autocombustion Method