Growth temperature dependent structural and magnetic properties of epitaxial Co{sub 2}FeAl Heusler alloy films
Journal Article
·
· Journal of Applied Physics
- State Key Laboratory of Superlattices and Microstructures, Institute of Semiconductors, Chinese Academy of Sciences, P.O. Box 912, Beijing 100083 (China)
The structural and magnetic properties of a series of Co{sub 2}FeAl Heusler alloy films grown on GaAs(001) substrate by molecular beam epitaxy have been studied. The epitaxial Co{sub 2}FeAl films with an ordered L{sub 21} structure have been successfully obtained at growth temperature of 433 K, with an in-plane cubic magnetic anisotropy superimposed with an unusual uniaxial magnetic anisotropy. With increasing growth temperature, the ordered L{sub 21} structure degrades. Meanwhile, the uniaxial anisotropy decreases and eventually disappears above 673 K. The interfacial bonding between As and Co or Fe atom is suggested to be responsible for the additional uniaxial anisotropy.
- OSTI ID:
- 22163057
- Journal Information:
- Journal of Applied Physics, Vol. 113, Issue 23; Other Information: (c) 2013 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0021-8979
- Country of Publication:
- United States
- Language:
- English
Similar Records
Co{sub 2}FeAl Heusler thin films grown on Si and MgO substrates: Annealing temperature effect
Temperature dependent magnetic anisotropy of epitaxial Co{sub 2}FeAl films grown on GaAs
Epitaxial films of Heusler compound Co{sub 2}FeAl{sub 0.5}Si{sub 0.5} with high crystalline quality grown by off-axis sputtering
Journal Article
·
Tue Jan 28 00:00:00 EST 2014
· Journal of Applied Physics
·
OSTI ID:22163057
+3 more
Temperature dependent magnetic anisotropy of epitaxial Co{sub 2}FeAl films grown on GaAs
Journal Article
·
Sat Mar 07 00:00:00 EST 2015
· Journal of Applied Physics
·
OSTI ID:22163057
+1 more
Epitaxial films of Heusler compound Co{sub 2}FeAl{sub 0.5}Si{sub 0.5} with high crystalline quality grown by off-axis sputtering
Journal Article
·
Mon Oct 14 00:00:00 EDT 2013
· Applied Physics Letters
·
OSTI ID:22163057
+5 more