Title: Effect of composition on electrical properties of lead-free Bi{sub 0.5}(Na{sub 0.80}K{sub 0.20}){sub 0.5}TiO{sub 3}-(Ba{sub 0.98}Nd{sub 0.02})TiO{sub 3} piezoelectric ceramics

Lead-free piezoelectric ceramics with the composition of (1-x)Bi{sub 0.5}(Na{sub 0.80}K{sub 0.20}){sub 0.5}TiO{sub 3}-x(Ba{sub 0.98}Nd{sub 0.02})TiO{sub 3} or (1-x) BNKT-xBNdT (with x = 0-0.20 mol fraction) have been synthesized by a conventional mixed-oxide method. The compositional dependence of phase structure and electrical properties of the ceramics were systemically studied. The optimum sintering temperature of all BNKT-BNdT ceramics was found to be 1125 Degree-Sign C. X-ray diffraction pattern suggested that BNdT effectively diffused into BNKT lattice during sintering to form a solid solution with a perovskite structure. Scanning electron micrographs showed a slight reduction of grain size when BNdT was added. It was found that BNKT-0.10BNdT ceramic exhibited optimum electrical properties ({epsilon}{sub r} = 1716, tan{delta} = 0.0701, T{sub c} = 327 Degree-Sign C, and d{sub 33} = 211 pC/N), suggesting that this composition has a potential to be one of a promising lead-free piezoelectric candidate for dielectric and piezoelectric applications.
Authors:
 [1] ; ;  [1] ;  [2]
  1. Department of Physics and Materials Science, Faculty of Science, Chiang Mai University, Chiang Mai 50200 (Thailand)
  2. (Thailand)
Publication Date:
OSTI Identifier:
22122808
Resource Type:
Journal Article
Resource Relation:
Journal Name: Journal of Applied Physics; Journal Volume: 114; Journal Issue: 2; Other Information: (c) 2013 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
36 MATERIALS SCIENCE; 75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND SUPERFLUIDITY; BARIUM COMPOUNDS; BISMUTH COMPOUNDS; CERAMICS; DIELECTRIC MATERIALS; DIFFUSION; GRAIN SIZE; NEODYMIUM COMPOUNDS; PERMITTIVITY; PEROVSKITE; PIEZOELECTRICITY; POTASSIUM COMPOUNDS; SCANNING ELECTRON MICROSCOPY; SINTERING; SODIUM COMPOUNDS; SOLID SOLUTIONS; TITANATES; X-RAY DIFFRACTION