Synthesis of nanocrystalline thin films of gold on the surface of GaSb by swift heavy ion
- Department of Physics, University of Mumbai, Santacruz (E), Mumbai-400 098 (India)
Thin films of gold ({approx}100 nm thick) were deposited on p-type GaSb substrates. These samples were irradiated with 100 MeV Fe{sup 7+}ions for the fluence of 1 Multiplication-Sign 10{sup 13} and 1 Multiplication-Sign 10{sup 14} ions cm{sup -2}. After irradiation, samples were characterized using AFM, UV-VIS -NIR, X-Ray Diffraction techniques. AFM studies showed the presence of clusters on the surface of GaSb. R.M.S. roughness of the sample was found to increase w.r.t ion fluence. Absorption coefficient obtained from the Ultra violet - Visible NIR (UV-VIS -NIR) spectra of the samples irradiated with various fluences compared with non irradiated GaSb. The annealing experiment showed a significant improvement in the absorption coefficient after rapid thermal annealing at temperature of 400 Degree-Sign C. X-Ray Diffraction study reveals different orientations of Au film.
- OSTI ID:
- 22113502
- Journal Information:
- AIP Conference Proceedings, Vol. 1512, Issue 1; Conference: 57. DAE solid state physics symposium 2012, Mumbai (India), 3-7 Dec 2012; Other Information: (c) 2013 American Institute of Physics; Country of input: International Atomic Energy Agency (IAEA); ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Synthesis Of Noble Metal Nanoparticle Composite Glasses Using Low Energy Ion Beam Mixing
Investigation on optical absorption properties of ion irradiated single walled carbon nanotubes
Related Subjects
77 NANOSCIENCE AND NANOTECHNOLOGY
ABSORPTION SPECTROSCOPY
ANNEALING
ATOMIC FORCE MICROSCOPY
CRYSTALS
DEPOSITION
GALLIUM ANTIMONIDES
GOLD
INFRARED SPECTRA
ION BEAMS
IRON IONS
IRRADIATION
MEV RANGE
NANOSTRUCTURES
PHYSICAL RADIATION EFFECTS
ROUGHNESS
SUBSTRATES
THIN FILMS
ULTRAVIOLET SPECTRA
VISIBLE SPECTRA
X-RAY DIFFRACTION