Title: Synthesis, crystal structure and photoluminescence of a new Eu-doped Sr containing sialon (Sr{sub 0.94}Eu{sub 0.06})(Al{sub 0.3}Si{sub 0.7}){sub 4}(N{sub 0.8}O{sub 0.2}){sub 6}

Colorless transparent platelet single crystals of a novel Eu{sup 2+}-doped strontium silicon aluminum oxynitride, (Sr{sub 0.94}Eu{sub 0.06})(Al{sub 0.3}Si{sub 0.7}){sub 4}(N{sub 0.8}O{sub 0.2}){sub 6}, were prepared at 1800 Degree-Sign C and 0.92 MPa of N{sub 2}. Fundamental reflections of electron and X-ray diffraction of the crystals were indexed with a face-centered orthorhombic unit cell (a=5.8061(5) A, b=37.762(3) A, c=9.5936(9) A). Diffuse streaks elongated in the b-axis direction were observed around the fundamental reflections hkl with h=2n+1 of the electron and X-ray diffraction, indicating stacking faults of (0 1 0)[1 0 0]/2. A crystal structure model without the stacking faults was obtained using the X-ray diffraction data of the fundamental reflections with the space group Fdd2. A SiN{sub 4}-tetrahedron double layer of [SiN{sub 2}]{sub 2} and a Sr/Eu double layer of [(Sr{sub 0.94}Eu{sub 0.06})Al{sub 1.2}Si{sub 0.8}N{sub 0.8} O{sub 1.2}]{sub 2} are stacked alternately along the b-axis direction. The title compound showed an emission with a peak wavelength of 490 nm under 334 nm excitation at room temperature. - Graphical abstract: Single crystals of a novel Eu{sup 2+}-doped strontium silicon aluminum oxynitride, (Sr{sub 0.94}Eu{sub 0.06})(Al{sub 0.3}Si{sub 0.7}){sub 4}(N{sub 0.8}O{sub 0.2}){sub 6}, having stacking faults on the (0 1 0) plane of an orthorhombicmore » cell, were prepared at 1800 Degree-Sign C and 0.92 MPa of N{sub 2}. The compound showed emission with a peak wavelength of 490 nm under 334 nm excitation at room temperature. Highlights: Black-Right-Pointing-Pointer A new compound Eu{sup 2+}-doped (Sr{sub 0.94}Eu{sub 0.06})(Al{sub 0.3}Si{sub 0.7}){sub 4}(N{sub 0.8}O{sub 0.2}){sub 6} was prepared. Black-Right-Pointing-Pointer Stacking faults in the compound were clarified by electron and X-ray diffraction. Black-Right-Pointing-Pointer A basic crystal structure model was obtained based on the X-ray diffraction data. Black-Right-Pointing-Pointer An emission of 490 nm under 334 nm excitation at room temperature was observed.« less
Authors:
 [1] ; ;  [2]
  1. Institute of Multidisciplinary Research for Advanced Materials, Tohoku University 2-1-1 Katahira, Aoba-ku, Sendai 980-8577 (Japan)
  2. Mitsubishi Chemical Group, Science and Technology Research Center, Inc. 1000 Kamoshida-cho, Aoba-ku, Yokohama 227-8502 (Japan)
Publication Date:
OSTI Identifier:
22012157
Resource Type:
Journal Article
Resource Relation:
Journal Name: Journal of Solid State Chemistry; Journal Volume: . 190; Other Information: Copyright (c) 2012 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
37 INORGANIC, ORGANIC, PHYSICAL AND ANALYTICAL CHEMISTRY; ALUMINIUM; ALUMINIUM OXIDES; DOPED MATERIALS; EUROPIUM IONS; EXCITATION; LAYERS; MONOCRYSTALS; ORTHORHOMBIC LATTICES; PEAKS; PHOTOLUMINESCENCE; REFLECTION; SILICON; SILICON NITRIDES; SPACE GROUPS; STACKING FAULTS; STRONTIUM; SYNTHESIS; X-RAY DIFFRACTION